Solvent-Based Hydroxyl Acrylic Polyol Resin

SE6670M Solvent-Based Hydroxyl Acrylic Polyol Resin 2k Automobile Refinishing Paint

Product Introduction

SE6670M is a solvent-based acrylic polyol resin with 3.0% hydroxyl content (based on the theoretical calculation of non-volatile components). It is used to prepare solvent-based two-component polyurethane coatings mixed with aliphatic isocyanate curing agent. It is suitable for cement permeable paint, anticorrosive paint, PU finish paint and floor paint.

Physical Property

Performance

High gloss, good leveling property;

Excellent chemical resistance;

Fast drying speed, high hardness.

Application

It is mainly used in combination with Desmodur N75, N3390, N3600 and other curing agents, and can be used to prepare self-drying or low-temperature baking cement permeable paint, anticorrosive paint, PU finish paint and floor paint.

Storage

The resin should be stored indoors in original, unopened, undamaged container in a dry place at storagetemperature no more than 30ºC. Exposure to direct sunlight should be avoided.Under above mentioned storage condition, the shelf life ofthe resin will be 730 days after production.

Compatibility with resins and solvents

Note: + means soluble/miscible; ○ means partially soluble/partially miscible; -means insoluble/incompatible.

Reference recipe

Special Tips

This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.