Platinum Translucent Liquid Silicone Rubber For Mould Making 25 shore A Product description Two-components addition type silicone rubber is a two-part...
2024-12-09 21:01:25
|
|
..., liquid silicone system that cures (RTV) to a 25 Shore A rubber. The polymerization can be accelerated by heat. The silicone components are ...
2025-07-31 00:16:44
|
|
... Mix ratio (A:B) 1:1 Working time(at 25℃ ,minutes) 30-40 Curing time(at 25℃,hrs,approx.) 6 Hardness Shore A(after 24 h) 20 Tensile Strength(Mpa...
2024-12-09 20:27:56
|
|
...,approx.) 7000-9000 Mix ratio (A:B) 1:1 Working time(at 25℃ ,minutes) 30-40 Curing time(at 25℃,hrs,approx.) 6 Hardness Shore A(after 24 h) 20 ...
2024-12-09 20:59:24
|
|
... at room temperature. The polymerization can be accelerated by heat (max.1500 C). The silicone components are delivered as liquids, which once ...
2025-03-30 13:27:55
|
|
...,approx.) 7000-9000 Mix ratio (A:B) 1:1 Working time(at 25℃ ,minutes) 30~40 Curing time(at 25℃,hrs,approx.) 4~6 Hardness Shore A(after 24 h) 30 ...
2025-07-31 00:16:44
|
|
..., liquid silicone system that cures (RTV) to a Shore A 5~55 rubber. The polymerization can be accelerated by heat. The silicone components are ...
2025-07-31 00:16:44
|
|
... at room temperature.The polymerization can be accelerated by heat (max. 150 C). The silicone components are delivered as liquids, which once mixed ...
2025-06-21 02:28:16
|
|
... at room temperature.The polymerization can be accelerated by heat (max. 150 C). The silicone components are delivered as liquids, which once mixed ...
2025-06-21 02:28:13
|
|
...minutes) 30-40 Curing time(at 25℃,hrs,approx.) 4~6 Hardness Shore A(after 24 h) 15 Tensile Strength(Mpa,after 24 h) 3.8 Elongation(%) 580 Tear ...