Prime Quality Astm Ss 410 430 Stainless Steel Round Rod Bar

304
304 stainless steel is a common material in stainless steel with a density of 7.93 g/cm, also known in the industry as 18/8 stainless steel.High temperature resistance 800℃, with the characteristics of good processing performance, high toughness, widely used in the industrial and furniture decoration industry and food and medical industry.
Tensile strength b (MPa)≥515-1035
304 stainless steel atlas
304 stainless steel atlas (6 sheets)
The yield strength is 0.2 (MPa)≥205
Elongation = 5 (%)≥40
Reduction of area bits of p (%)?
Hardness: 201 HBW or less;
92 HRB or less;
210 hv or less
Density (20℃, g/cm) : 7.93
Melting point (℃) : 1398~1454
Specific heat capacity (0~100℃, KJ· kg-1k-1) : 0.50
Thermal conductivity (W·m-1· k-1) :(100℃) 16.3, (500℃) 21.5
Linear expansion coefficient (10-6· k-1) :(0~100℃) 17.2, (0~500℃) 18.4
Resistivity (20 ℃, 10-6 Ω m2 / m) : 0.73
Longitudinal modulus of elasticity (20℃, KN/mm2) : 193

304L
304L stainless steel, also known as ultra-low carbon stainless steel, is a universal stainless steel material, widely used in the production of good comprehensive performance (corrosion resistance and formability) equipment and components.
C:≤0.03 ,
Si :≤1.0 ,
Mn :≤2.0 ,
Cr :18.0～20.0 ,
Ni :9.0～12.0,304
304 stainless steel is a common material in stainless steel with a density of 7.93 g/cm, also known in the industry as 18/8 stainless steel.High temperature resistance 800℃, with the characteristics of good processing performance, high toughness, widely used in the industrial and furniture decoration industry and food and medical industry.
Tensile strength b (MPa)≥515-1035
304 stainless steel atlas
304 stainless steel atlas (6 sheets)
The yield strength is 0.2 (MPa)≥205
Elongation = 5 (%)≥40
Reduction of area bits of p (%)?
Hardness: 201 HBW or less;
92 HRB or less;
210 hv or less
Density (20℃, g/cm) : 7.93
Melting point (℃) : 1398~1454
Specific heat capacity (0~100℃, KJ· kg-1k-1) : 0.50
Thermal conductivity (W·m-1· k-1) :(100℃) 16.3, (500℃) 21.5
Linear expansion coefficient (10-6· k-1) :(0~100℃) 17.2, (0~500℃) 18.4
Resistivity (20 ℃, 10-6 Ω m2 / m) : 0.73
Longitudinal modulus of elasticity (20℃, KN/mm2) : 193

304L
304L stainless steel, also known as ultra-low carbon stainless steel, is a universal stainless steel material, widely used in the production of good comprehensive performance (corrosion resistance and formability) equipment and components.
C:≤0.03 ,
Si :≤1.0 ,
Mn :≤2.0 ,
Cr :18.0～20.0 ,
Ni :9.0～12.0,
S :≤0.03 ,
P :≤0.045
S :≤0.03 ,
P :≤0.045