Black Yellow 2K Polyurethane Adhesive Curing PU UH-3005

  • 1
  • 2
Brand Name WANLI-ADHESION
Model Number UH®-3005
Certification ISO9001 ISO14001 IATF16949
Place of Origin CHINA
Minimum Order Quantity 400 ml
Payment Terms L/C, T/T
Delivery Time 5-8 work days
Packaging Details 400 ml/Tube, 23L/Barrel, 195L/Barrel
performance Component A: UH®-3005 A/ Component B:UH®-3005 B
Fundamentals of Chemistry Component A: Polyol/ Component B: Isocyanate
colour(Before mixing） Component A: black / Component B: canary yellow
colour(After mixing） black
Curing mechanism Addition polymerization
Density（ kg/l）(Before mixing） Component A: 1.44 / Component B: 1.33
Density（ kg/l）(After mixing） 1.385
Mixing ratio (A: B volume ratio) 100 : 100
Mixing ratio (A: B weight ratio) 100 : 92.5
Viscosity (brookfleld 7# rotor 10rpm25 ℃) Component A: about 30000CPS / Component B: about 20000CPS
Applicable period (min) 35A
Shore D hardness (ASTM D2240) 60
Tensile strength (ASTM D638 MPa) 10
Thermal conductivity (ASTM e1461 w/ (m · K)) 0.5
Elongation at break (ASTM D638) 5-10 %
Shear strength (ASTM d1002 aluminum 3003- aluminum 3003 MPa) 14.6
working temperature -40 – 80 °C
Detailed Product Description

 2K Polyurethane Adhesive UH®-3005

 

UH®-3005 is a two-component room temperature curing polyurethane adhesive. UH®-3005 is a semi-structural elastic adhesive, which can be bonded to a variety of substrates.

 

APPLICATION

UH®-3005 is designed for high strength bond bonding of a variety of substrates, including fiberglass, painted metal and plastics. This product is only for users with professional skills. In order to verify the bonding effect and the compatibility of the product with the material, tests should be carried out in advance on the actual substrate and environment.

 

SpecUH®-3005 AUH®-3005 B
AppearanceBlack(Before Mixing)Yellow(Before Mixing)
Black(After Mixing)
ComponentPolyolIsocyanate
Curing MechanismAddition Polymerization
Density(Kg/l)1.44(Before Mixing)1.33(Before Mixing)
1.385(After Mixing)
Mixing RatioA:B(Volume Ratio)=100:100
A:B(Weight Ratio)=100:92.5
ViscosityAbout 30000CPSAbout 20000CPS
(Brookfleld 7# Rotor 10rpm25℃)
Applicable Period (min)35A
Shore D Hardness60(ASTM D2240)
Tensile Strength10(ASTM D638 MPa)
Thermal Conductivity0.5(ASTM E1461 W/ (m · K))
Elongation At Break5~10%(ASTM D638)
Shear Strength14.6(ASTM D1002 Aluminum 3003- Aluminum 3003 MPa)
Working Temperature-40 – 80 °C
Shelf Life6 Months
Package400 ml/Tube, 23L/Barrel, 195L/Barrel

 

FEATURE

Good construction performance

Long operating time

High strength

high elasticity

excellent resistance to dynamic loads

 

Curing Mechanism

UH ®- 3005 is cured by a two-component chemical reaction.

High temperature can accelerate the curing speed, while low temperature will slow down the curing speed.

 

Chemical Resistance

If it is used in thermal environment or chemical environment, we suggest to carry out relevant project test, please contact wanli bonding technology department.

 

  

 

 
Product Tags: black 2K Polyurethane Adhesive   yellow 2K Polyurethane Adhesive   curing 2k pu adhesive  
Related Products
Distinctive 2KPU-802 Polyurethane Adhesive 700 MPa.S for sale

Distinctive 2KPU-802 Polyurethane Adhesive 700 MPa.S

Black Yellow 2K Polyurethane Adhesive Curing PU UH-3005 for sale

Black Yellow 2K Polyurethane Adhesive Curing PU UH-3005

Email to this supplier
 
From:
Enter your Email please.
To: WUXI WANLI ADHESION MATERIALS CO., LTD.
Subject:
Message:
Characters Remaining: (80/3000)
 
Home | Products | Suppliers | About Us | 公司概况
Terms of user - Intellectual Property Rights (IPR) Protection Policy - Privace Policy
Copyright © 2011-2026 everychina.com.cn. All rights reserved.