Thermal Vulcanization Adhesive Bonding Agent For Rubber Industry Double Coat
|
Detailed Product Description
|
Thermal Vulcanization Adhesive Bonding Agent for Rubber Industry
Double Coat Lorechem Thinkbond thermal vulcanization adhesive with high bond
strength, stable quality, easy to use, and widely used in a variety
of rubber and metal bonding.
Cover coat:
Applying Thinkbond: Agitation: We recommend stir Thinkbond adhesive before the application
to avoid settle down. Brushing: Application by brushing is normally undertaken without further
dilution, but for coating large areas, dilution with MEK (or the
diluent blend shown below) improves flow and speed of application. Spraying: We recommend an HVLP gun using 1.5 Bar air-pressure and a nozzle
size of 1 -1.5mm. For this application we recommend diluting
between 50 and 100% v/v. Roller coating: Dilute to 35 - 45 seconds on a DIN 4 or Ford 4 cup at 25 C for
most roller application processes. Dilution with a high boiling
solvent like MPA may be necessary to achieve the best finish and to
reduce the skinning of the bonding agent in the applicator. Drying: Dry the film between 10 and 30 minutes at room temperature. If it
is necessary to reduce drying time, we recommend to use forced air
for 5 minutes at 100ºC maximum. Do not use in this stage
temperatures above 100ºC to avoid adhesive pre-cure. After this
process, follow to cure. Thickness of application layer: The layer thickness must be between 15 and 25 µm. For severe environments or dynamic fatigue applications, use ≧25
microns. Under these conditions it is possible to achieve bonds
with no edge-failure after 400 hour salt-spray tests Parts with Thinkbond adhesive already applied can be stored for 30
days prior to cure.
Storage: Keep container tightly closed during storage and always keep away
from heat sources. Store in an environment below 10ºC increases the
shelf life of the adhesive. More Thinkbond adhesive for PU and rubber:
|
||||||||||||||||||||
| Product Tags: Thermal Vulcanization Adhesive Bonding Agent Rubber Industry Adhesive Bonding Agent Double Coat mould release agent |
Related Products
|
Thermal Vulcanization Adhesive Bonding Agent For Rubber Industry Double Coat |
|
Liquid State Solvent Based Rubber Adhesive Silicone Rubber To Metal Bonding Agent |
|
Solvent Diluent Car Interior Trim Adhesive Liquid State Environmentally Friendly |
|
Solvent Based Double Coat Rubber Adhesive, Rubber Bonding Glue For NBR Seals |
|
Clear One Component Solvent Based Bonding Agent For CPU/MPU/TPU |
|
Non-Toxic Thermoset Adhesive Bonding Agent for NBR CR ACM ECO Rubber to Metal |
Email to this supplier