THINKBOND Hot Vulcanization Adhesive for Automotive Engine Seals
Application Field:
It is an adhesive for automotive engine seals.
THINKBOND hot vulcanization adhesive is mainly used for bonding special rubber with various metal and non-metal substrates, used in various rubber, fluorine rubber, fluorine silicone, AEM, ACM, HNBR and various metals, engineering plastics, fiber fabrics and other non-metal hot vulcanization adhesive, It has good static bonding properties, excellent dynamic fatigue resistance, good solubility resistance, high and low temperature resistance. For example, high peeling strength, long-term salt spray corrosion resistance and boiling water cooking resistance, in line with environmental requirements.
Application:
Applying Thinkbond:
Agitation: We recommend stir Thinkbond adhesive before the application
to avoid settle down. Brushing: Application by brushing is normally undertaken without further
dilution, but for coating large areas, dilution with MEK (or the
diluent blend shown below) improves flow and speed of application. Spraying: We recommend an HVLP gun using 1.5 Bar air-pressure and a nozzle
size of 1 -1.5mm. For this application we recommend diluting
between 50 and 100% v/v. Roller coating: Dilute to 35 - 45 seconds on a DIN 4 or Ford 4 cup at 25 C for
most roller application processes. Dilution with a high boiling
solvent like MPA may be necessary to achieve the best finish and to
reduce the skinning of the bonding agent in the applicator. Drying: Dry the film between 10 and 30 minutes at room temperature. If it
is necessary to reduce drying time, we recommend to use forced air
for 5 minutes at 100ºC maximum. Do not use in this stage
temperatures above 100ºC to avoid adhesive pre-cure. After this
process, follow to cure. Thickness of application layer: The film obtained by applying Thinkbond adhesive. The layer thickness must be between 15 and 25 µm. For severe environments or dynamic fatigue applications, use ≧25
microns. Under these conditions it is possible to achieve bonds
with no edge-failure after 400 hour salt-spray tests Parts with Thinkbond adhesive already applied can be stored
for 30 days prior to cure.
Storage: Keep container tightly closed during storage and always keep away
from heat sources. Store in an environment below 10ºC increases the
shelf life of the adhesive.
Shanghai LoreChem Co., Ltd. was established in 2008. It is a
high-tech enterprise which is dedicated to serve releasing products
which involve semi-permanent release agent, anti-sticking, surface
lubrication and thermal reactive adhesive. Shanghai LoreChem has
been improving product quality for 15 years. The releasing products
are mainly applied in rubber, polyurethane and composite industry.
The brand of Lubekote for release agent and Thinkbond for adhesive
have been registered in China. Both of them are well known in the
industry. |
||||||||||||||||||||
| Product Tags: Solvent Based Hot Vulcanization Adhesive Thinkbond Hot Vulcanization Adhesive Engine Seals Hot Vulcanization Adhesive |
|
Thermal Vulcanization Adhesive Bonding Agent For Rubber Industry Double Coat |
|
Non-Toxic Thermoset Adhesive Bonding Agent for NBR CR ACM ECO Rubber to Metal |
|
Clear One Component Solvent Based Bonding Agent For CPU/MPU/TPU |
|
Lead Free Liquid Form Rubber Adhesive , Bonding Agent For Rubber To Metal |
|
Rubber Bonding Agent Grey Liquid 0.92-0.96 G/Cm3 Density Environmentally friendly |
|
Liquid State Solvent Based Rubber Adhesive Silicone Rubber To Metal Bonding Agent |