J100 Polymer Modified Cementitious Waterproof Coating
|
|
Joaboa Tech Coating Series
J100 is a high-grade waterproof coating carefully developed by Joaboa Tech. The product is made of high quality polymer emulsion and selected additives according to scientific ratio. When the polymer emulsion is mixed with cement, the chemical reaction that takes place can form a tough elastic waterproof film, lasting and effective waterproof.
18kg per pail ※ Material Features1. Good Bonding Strength
J100 polymer modified cementitious waterproofing coating can be applied on dry or wet base surface, with good adhesion.
2. Composite Use
J100 polymer modified cement waterproofing can be used with a variety of other waterproof coatings or waterproofing membranes, suitable for different levels of waterproof engineering.
3. Strong Water Resistance
Compared with similar products, JS polymer modified cementitious coating has good water resistance and durable waterproof effect.
4. Environment-friendly
J100 acrylic polymer modified cementitious coating does not pollute the environment and is harmless to human body. It can be used for waterproof engineering of drinking pool.
5. Cost-effective
Ratio of Material Weight during Application as J100 Coating : Cement=1:1, no need to purchase powdery materials from Joaboa Tech. That means it can reduce the cost greatly.
※ Scope of Application
1) JS acrylic polymer cementitious coating is applicable to inner and outer wall, kitchen, toilet, balcony, terrace, roof and other non-exposed waterproof works. 2) Suitable for basement, swimming pool, pool and other parts of the waterproof, seepage engineering.
※ Construction Requirments
1. Make sure substrates are leveled, firm, clean and no visual
water on the surface. Any cracks should be repaired first. Internal
& external corners need to camber.And dry substrates should be
moistened. 2. If necessary, mix emulsion with water at the weight ratio of
1:1, then brush the mixture on the substrates. 3. Add cement into the J100 Coating slowly, stir the mixture evenly with
electric mixer for 5 mins. Proportioning of waterproofing coating: Weigh materials as
emulsion/cement=1/1. 4. Brush thinly for several times with scraper evenly. The next
brushing of acrylic cementitious waterproofing coating should conduct after the prior becomes surface dry. 5. Application method with fiberglass mesh: generally,
J100 acrylic polymer modified cementitious coating needs two
times brushing. Place the fiberglassmesh after the first brushing,
and keep it leveled. Do the second time brushing after the prior
coating filmbecomes surface dry but not hard dry.
※ Construction MethodsJS Polymer Modified Cement Waterproofing Coating can use construction methods as below: brushing, roller coating, spraying, etc.
※ Packing MethodProfessional loading method with wooden pallets to ensure the safety of J100 Polymer Cementitious Waterproof Coating during export.
※ Techinical Data Sheet of JS Polymer Cementitious Waterproofing Coating
※ Storage and Transport
1. J100 polymer cement based waterproof coating is non-flammable and explosive material, which can be transported as general goods. During transportation, it should be protected from sun protection, frost protection, rain protection, extrusion and collision. Keep the package intact. 2. J100 modified cement waterproofing shall be stored in a ventilated, dry and protected from direct sunlight. 3. J100 polymer cement waterproofing should be stored in the warehouse at the temperature within 5℃-35℃, and the shelf life of the product is 12 months. 4. Products of different types and specifications should be stacked separately and should not be mixed.
※ Market Share
Joaboa Tech, Inventor and Representative Brand of Chinese Self-adhesive Waterproof Membrane, acrylic polymer modified cementitious waterproofing, whose market share has ranked as Top 1 in Chinese domestic market for over 10 years, widely used in Viet Nam, Cambodia, India, etc. as well.
※ Document Download
|
| Product Tags: J100 polymer waterproof coating cementitious waterproof coating polymer modified waterproof sealant |