BS 3262 Standard Thermoplastic Road Marking Paint with 20% Glass
Beads Anti-slip Good Reflecitve
Description
Thermoplastic road marking paint is mainly used for more than 2
level road and highway.The thickness of lines made from this
coating is (1.0 ~ 4.0) mm, paint mixed with reflective glass beads,
and in the construction, spread the reflective glass beads on the
surface. This type of marking line has good nightly reflective
performance, long service life, generally up to2 ~ 3 years.
Thermoplastic road marking paint needs special heater device in
constructions. In second re-marking construction of old marking
lines, you should eliminate the thick old marking line firstly.
Technical Specification
Density(g/cm3) | 1.8-2.3 |
| Softening point (℃) | 90-125 |
| Compressive Strength(MPa) | ≥12 |
| Glass bead content(%) | 0-30% |
| Liquidity | 35±10 |
| Packing | 25kg/bag |
| Color | White/Yellow/Blue/Red/Green/Customized |
| Executive standard | JT/T280-2004/AASHTO/BS3262/Customized |
| Appearance | Powder |
| Construction temperature | 180℃-220℃ |
| Whiteness | 70-85(Customized) |
| Inverse coefficient | 50-550 |
| Warranty | 12 months |
| Storage Method | Avoid light and moisture |
| Packing Size | 45×70×5CM |
Advantages of Thermoplastic Road Marking Paint
•Good use effect& quick-drying
①The coating film of hot melt paint has complete clear lines, sharp
edges and corners, high vividness and three dimensional effect.
②It can be dry and open to traffic 1-3 minutes after painting, and
construction can even be carried out without blocking
traffic.
•Excellent wear resistance& Reflective at night
①The coating film of this paint is durable and the service life of
the marking can up to 2 years. Stronger adhesion, Good liquidity,
stronger weather resistance, high compressive strength..
②Since the paint is mixed with glass beads, marking coating is
strong reflection at night, traffic accidents can be reduce
Formula Customized
|
Customized Formula |
| Customized Formula | Content(Customized range) | Characteristics |
| C5 Resin | 10%-22% | Fluidity Toughness Hardness Adhesion |
| Titanium Dioxide | 0.5-10% | 0.5%-30% |
| Premixed glass beads | 0%-30% | Reflective after surface wear |
| Calcium Carbonate Sand | 30%-80% | Whiteness Wear-resistant Hardness |
| PE Wax | 1%-1.5% | Cold and heat resistant |
| EVA | 0.5%-1% | Crack resistance |
| Plasticizer | 1%-1.5% | Toughness |