Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility

  • 1
  • 2
  • 3
  • 4
Brand Name LEOTECH
Model Number UT-ML
Certification CE
Place of Origin Chongqing, China
Minimum Order Quantity 500 pcs
Price $39.58/piece
Payment Terms T/T
Product Name UT-ML Dental Zirconia Block
Product Specification 98, 95, 92*75*16 mm
Thickness 16 mm
Prices 39.58
Power Source Manual
Warranty 1 Year
After-sale Service Online technical support
Shelf Life 1 year
Quality Certification ce
Instrument classification Class II
Detailed Product Description
Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility
UT-ML Dental Zirconia Block
● High Strength ● High Transparency ● Natural






UT-ML: Superior Zirconia for Demanding Restorations
Outperforms standard grades:

  • High Translucency: 53% (1 mm)

  • Low Thermal Expansion: (10.5 ± 0.5) × 10⁻⁶ K⁻¹

  • Aging Resistance: <5% monoclinic phase post-acceleration
    Perfect for aesthetic anterior crowns and bridges.


Product Parameters:
ModelUT Multilayer 95mm
Size95mm
Strength600-800 MPa
Shades16 VITA Classical.
Disc Sizes9 thicknesses(10,12.14.16.18.20.22.25.30mm)
 



Technical Parameters:

1.Chemical composition

ComponentsUT-ML
ZrO2+HfO2+Y2O3≥99%
Y2O38.0%-10.0%
Al2O3＜0.15%
Other Oxides＜0.5%

2.Physical characteristics

PropertiesUT-ML
Density before sintering(g.cm-3)3.15±0.05
Density after sintering(g.cm-3)6.06±0.02
CTE(25-500℃)(K-1)(10.5±0.5)×10-6
Flexural strength after sintering(Mpa)600-800
Translucency(1.0±0.02mm)49%-53%
Fracture toughness(MPa.m1/2)3.5-5.0
Hardness(HV10)1150-1250
Accelerated aging surface monoclinic phase content＜5%
Chemical solubility after sintering(μg.cm-2)＜100
Cytotoxicity0 Level
Radioactivity(Bq.g-1)＜0.1
Sintering temperature(℃)1480-1510
Recommend 1500

Indications For Use ≤3 units



Sintering:



 







 
Product Tags: Sintering Zirconia   Low Temperature Sintering Zirconia  
Related Products
Low-Temp Zirconia UT-ML 1480-1510℃ Range 1150-1250 HV10 3-Unit Bridges for sale

Low-Temp Zirconia UT-ML 1480-1510℃ Range 1150-1250 HV10 3-Unit Bridges <100μg/cm² Solubility

UT-ML Dental Disc 1500℃ Fast Sintering 49-53% Translucency ≤3-Unit Crown / Bridge 0 Cytotoxicity for sale

UT-ML Dental Disc 1500℃ Fast Sintering 49-53% Translucency ≤3-Unit Crown / Bridge 0 Cytotoxicity

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM for sale

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 for sale

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

Dental Zirconia for Crown / Bridge 49-53% Light Transmission 1500℃ Sintering Class 0 Cytotoxicity for sale

Dental Zirconia for Crown / Bridge 49-53% Light Transmission 1500℃ Sintering Class 0 Cytotoxicity

Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis for sale

Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility

Email to this supplier
 
From:
Enter your Email please.
To: Chongqing Leomed Technology Co., Ltd.
Subject:
Message:
Characters Remaining: (80/3000)
 
Home | Products | Suppliers | About Us | 公司概况
Terms of user - Intellectual Property Rights (IPR) Protection Policy - Privace Policy
Copyright © 2011-2025 everychina.com.cn. All rights reserved.