Dental Crown Zirconia 49-53% Translucency 600-800MPa Flexural Strength ISO 0 Cytotoxicity

Browse Categories

Chongqing Leomed Technology Co., Ltd.

City: chongqing

Province/State:chongqing

Country/Region:china

Tel:86--18983289817

Contact Person:
Mr.Jason Chen View Contact Details

Dental Crown Zirconia 49-53% Translucency 600-800MPa Flexural Strength ISO 0 Cytotoxicity

Brand Name	LEOTECH
Model Number	UT-ML
Certification	CE
Place of Origin	Chongqing, China
Minimum Order Quantity	500 pcs
Price	36.11
Payment Terms	T/T
Product Name	UT-ML Dental Zirconia Block
Product Specification	98, 95, 927514 mm
Thickness	14 mm
Power Source	Manual
Warranty	1 Year
After-sale Service	Online technical support
Shelf Life	1 year
Quality Certification	ce
Instrument classification	Class II

Detailed Product Description

Dental Crown Zirconia 49-53% Translucency 600-800MPa Flexural Strength ISO 0 Cytotoxicity

UT-ML Dental Zirconia Block

● High Strength ● High Transparency ● Natural

Optimized Sintering for UT-ML Zirconia
Sinter at 1500°C (range: 1480–1510°C) for high density (6.06 g/cm³) and efficiency. Low chemical solubility (<100 μg/cm²) and hardness (1150–1250 HV10) ensure precision. Ideal for labs prioritizing workflow and material performance.

Product Parameters:

Model	UT Multilayer 95mm
Size	95mm
Strength	600-800 MPa
Shades	16 VITA Classical.
Disc Sizes	9 thicknesses(10,12.14.16.18.20.22.25.30mm)

Technical Parameters:

1.Chemical composition

Components	UT-ML
ZrO2+HfO2+Y2O3	≥99%
Y2O3	8.0%-10.0%
Al2O3	＜0.15%
Other Oxides	＜0.5%

2.Physical characteristics

Properties	UT-ML
Density before sintering(g.cm-3)	3.15±0.05
Density after sintering(g.cm-3)	6.06±0.02
CTE(25-500℃)(K-1)	(10.5±0.5)×10-6
Flexural strength after sintering(Mpa)	600-800
Translucency(1.0±0.02mm)	49%-53%
Fracture toughness(MPa.m1/2)	3.5-5.0
Hardness(HV10)	1150-1250
Accelerated aging surface monoclinic phase content	＜5%
Chemical solubility after sintering(μg.cm-2)	＜100
Cytotoxicity	0 Level
Radioactivity(Bq.g-1)	＜0.1
Sintering temperature(℃)	1480-1510 Recommend 1500

Indications For Use ≤3 units

Sintering:

Factory Display:

Application:

Product Tags: ISO Dental Crown Zirconia Translucency Dental Crown Zirconia Cytotoxicity Dental Crown Zirconia

Related Products

Low-Temp Zirconia UT-ML 1480-1510℃ Range 1150-1250 HV10 3-Unit Bridges for sale

Low-Temp Zirconia UT-ML 1480-1510℃ Range 1150-1250 HV10 3-Unit Bridges <100μg/cm² Solubility

UT-ML Dental Disc 1500℃ Fast Sintering 49-53% Translucency ≤3-Unit Crown / Bridge 0 Cytotoxicity

Yttria-Stabilized Zirconia 8-10% 600-800MPa Flexural Strength ISO 6872 Certified Dental CAD/CAM

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 for sale

Low-Temp Sintered Zirconia Disc ≤3-Unit Prosthesis 1150-1250 HV10 <0.1 Bq/g Radioactivity

Dental Zirconia for Crown / Bridge 49-53% Light Transmission 1500℃ Sintering Class 0 Cytotoxicity

Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis for sale

Low-Temperature Sintering Zirconia 1480-1510℃ Range Dental Prosthesis <100μg/cm² Solubility

Email to this supplier


From:	Enter your Email please. Your email is incorrect!
To:	Chongqing Leomed Technology Co., Ltd.
Subject:	Subject is empty!
Message:	Characters Remaining: (80/3000) Please enter 20 to 3000 characters to contact this supplier!