0.05mm CuNi23 Resistance Copper Nickel Alloy Wire

Brand Name	TANKII
Model Number	CuNi23
Certification	ISO9001:2015
Place of Origin	Shanghai, China
Minimum Order Quantity	20kg
Price	Negotiation
Payment Terms	L/C, T/T, Western Union, Paypal
Supply Ability	200+TON+MONTH
Delivery Time	15-28DAYS
Packaging Details	Spool, carton, plywod case with plastic film as clients required
composition	Cu Bal, Ni 23%,Mn0.5%
shape	round wire
color	metallic
Carbon Content	low
Specification	0.05mm-8mm
Surface Treatment	Bright Annealed
density	8.9

Detailed Product Description

CuNi23 Resistance low temperature coefficient copper nickel binary alloy for heating cable of automobile heating cushion

Introduction
CuNi23 resistance alloy is one of copper nickel binary alloys, having low temperature coefficient of resistance. It is applied to make rheostat, shunt, controller and other low voltage electrical components with a maximum operating temperature of 300°C. Due to its good heat coefficient, this alloy is widely used in low temperature heating cable of automobile heating cushion, railway snow melting, etc.

Due to high tensile strength and increased resistivity values, the copper nickel alloy wires are the first choice for applications as resistance wires. With the different nickel amount in this product range, the characteristics of the wire can be chosen according to your requirements. Copper nickel alloy wires are available as bare wire, or enamelled wire with any insulation and self-bonding enamel. Furthermore, litz wire made of enamelled copper nickel alloy wire are available.

CuNi23Mn is a copper-nickel alloy (CuNi alloy) with medium resistivity for medium-low temperature resistances. The alloy is suitable for use at temperatures up to 400°C (750°F)

CuNi23Mn is very malleable and has a good resistance to corrosion until temperatures of 400°C. Ideal applications areas are all types of resistances used at low temperature.

CuNi23Mn is typically used in heating cables, fuses, resistors and various types of controllers.

Physical Data

Density 8.9 g/cm3

Specific Heat 0.37(J/kg 20°C)

Electrical Resistivity 0.03×10-6ohm.m

Melting Point 1150°C

Maximum Operating Temperature 400°C

Coefficient of linear expansion (coeff 10-6/°C) 15.7 from 20 to 1000°C

Typical Mechanical Properties

Mechanical Properties CuNi23

Tensile Strength 350 Mpa

Elongation 25%

Main Mechanical Properties:

		Cu	CuNi2	CuNi6	CuNi10	CuNi23Mn	CuNi44
Tensile strength	[N/mm²]	220-300	260-360	270-370	300-390	500-550	560-680
Yield strength at 1% elongation	[N/mm²]	120-200	140-240	160-220	140-250	200-330	400-500
Bending proof performance	[%]	100			160	760
Resistance (IACS)	[%]	101	34	17	12	6	3
Conductivity	[S*m/mm²]	58.5	20.0	10.0	6.7	3.33	2.0
Resistivity	[Ohm*mm²/m]	0.0171	0.05	0.10	0.1493	0.30	0.50
Thermal coefficient of resistance	[1E-6/K]	3900-4300	1100-1600	500-900	350-400	150-200	-80 - +40
Solderability	[-]	good	good	good	good	good	no conventional soldering

main property type		Cuni1	CuNI2	CuNI6	CuNi8	CuNI10	CuNi14	CuNi19	CuNi23	CuNi30	CuNi34	CuNI44
main chemical composition	Ni	1	2	6	8	10	14.2	19	23	30	34	44
	MN	/	/	/	/	/	0.3	0.5	0.5	1.0	1.0	1.0
	CU	rest	rest	rest	rest	rest	rest	rest	rest	rest	rest	rest
max working temperature		/	200	220	250	250	300	300	300	350	350	400
density g/cm3		8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9	8.9
resistivity at 20 °c		0.03 ± 10%	0.05± 10%	0.10± 10%	0.12± 10%	0.15± 10%	0.20± 5%	0.25± 5%	0.30± 5%	0.35± 5%	0.40± 5%	0.49± 5%
temperature coefficient of resistance		<100	<120	<60	<57	<50	<38	<25	<16	<10	-0	<-6
tensile strength mpa		>210	>220	>250	>270	>290	>310	>340	>350	>400	>400	>420
elongation		>25	>25	>25	>25	>25	>25	>25	>25	>25	>25	>25
melting point °c		1085	1090	1095	1097	1100	1115	1135	1150	1170	1180	1280
coefficient of conductivity		145	130	92	75	59	48	38	33	27	25	23

Product Tags: 0.05mm Copper Nickel Alloy Wire CuNi23 Copper Nickel Alloy Wire Annealed Copper Nickel Alloy Wire

Related Products

0.02mm To 10mm FeCrAl Alloy Resistance Wire Used For Heating Elements (CrAl 25/5)

Factory Polished Molybdenum Rod and Bar with >99.95% Purity for High Temperature Heating up to 2200ºC ASTM B386-91 Standard

Nichrome Heating Wire Ni80Cr20 0.018mm-1.6mm Diameter for sale


From:	Enter your Email please. Your email is incorrect!
To:	Shanghai Tankii Alloy Material Co.,Ltd
Subject:	Subject is empty!
Message:	Characters Remaining: (80/3000) Please enter 20 to 3000 characters to contact this supplier!

0.05mm CuNi23 Resistance Copper Nickel Alloy Wire

0.05mm CuNi23 Resistance Copper Nickel Alloy Wire

CuNi23Mn is a copper-nickel alloy (CuNi alloy) with medium resistivity for medium-low temperature resistances. The alloy is suitable for use at temperatures up to 400°C (750°F)

0.02mm To 10mm FeCrAl Alloy Resistance Wire Used For Heating Elements (CrAl 25/5)

Factory Polished Molybdenum Rod and Bar with >99.95% Purity for High Temperature Heating up to 2200ºC ASTM B386-91 Standard

Nichrome Heating Wire Ni80Cr20 0.018mm-1.6mm Diameter

Nickel 201 Alloy Wire UNS N02201 ASTM B160 B162

Ni80Cr20 Nichrome Alloy Flat Wire for High-Temperature Heating Elements

Ni200 Ni201 Pure Nickel Wire 99.98% High Purity 0.025-10mm