Anodized Aluminum Heatsink Extrusion Profiles , OEM Custom CNC
Machining Production Information
Alloy: | 6063 | 6061 | 6060 | 6005 | 6082 | | | | Temper : | T5 | T6 | T4 | | | | | | Standard: | DIN | AAMA | AS | CHINAGB | | | | | Certification: | ISO9001: 2008. | | Surface Finish: | Mill finish | Anodizing | Powder Coating | Wood Grain | Electrophoresis | Polished | Brushed | | Color: | Anodizing: | Silver, bronze, champagne, golden , etc. | | Anodizing thickness is up to 25um. | | Powder Coating: | White, black, bronze, grey, green, etc . | | Powder coating thickness is more than 60um. | | Electrophoresis: | Silver, nickel, golden yellow, black, champagne, etc | | Polishing | Silver, nickel, golden yellow, black, etc | | Brushing: | Silver, nickel, golden yellow, black, bronze, etc | | Machining: | Cutting, punching, drilling, bending, weld, mill, CNC, etc. | | OEM customized aluminium profiles are available. |
Technology Supports
- Engineering Design.
- Quality Standard: China GB, according to the Drawing and the
Customer's Details.
- Auto CAD.
Specifications:
1. Primary Technical Data
1)Chemical composition Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Impurity | Al | 6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.9 | 0.1 | 0.1 | 0.1 | 0.15 | Rest | 6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | 0.15 | Rest | 6060 | 0.3-0.6 | 0.1-0.3 | 0.1 | 0.1 | 0.35-0.6 | - | 0.15 | 0.1 | 0.15 | Rest | 6005 | 0.6-0.9 | 0.35 | 0.1 | 0.1 | 0.40-0.6 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
2) Mechanical property Alloy | Temper | Tensile strength | Yield strength | Elongation | 6063 | T5 | ≥ 160Mpa | ≥ 110Mpa | ≥ 8% | T6 | ≥ 205Mpa | ≥ 180Mpa | ≥ 8% | 6061 | T6 | ≥ 265Mpa | ≥ 245Mpa | ≥ 8% |
Competitive Advantage:
We can offer professional Manufacturing and exporting service,
OEM/ODM for Metal & Plastic parts in China. All the parts
manufactured by CNC Lathe & Milling Machine Center.
Tag : LED Aluminum Heat Sinkextruded aluminum heat sink |