Custom Made Aluminum Heatsink Extrusion Profiles For High Power Led
Light
Our Advantages:
1. 17+ years experience in providing ONE-STOP customized aluminium
extrusion and machining solution; 11+ years of exporting to 40+
countries;
2. ISO: 9001:2008, RoHS, SGS, Reach, D&B
4. 100% new material
5. Competitive prices with short lead-time for both tooling and
parts, because we do everything in-house
6. Effective and strong technical support (30+ engineers) and
excellent sales services .
7. Sufficient production capacity (22 extrusion lines; 3+ CNC
machines).
8. Efficient communication (48-hour quote lead time).
| Product name | Aluminium heat sink |
| Material | 6000 Series aluminium |
| Color | Different color available for your choices |
| Shape Size | According to customers' technical drawings |
| Surface finish | Mill finish, anodized, powder coated, electrophoresis, sand
balsting etc.and depend on customer's demand |
| Deep processing | Cutting ,punching,milling,drilling,welding,CNC |
| Used | Industry machinery |
Applications:
Aluminum heat sink is widely used on Machines , cars , lighter ...
Specifications:
1. Primary Technical Data
1)Chemical composition
Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Impurity | Al |
6063 | 0.2-0.6 | 0.35 | 0.1 | 0.1 | 0.45-0.9 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | 0.15 | Rest |
6060 | 0.3-0.6 | 0.1-0.3 | 0.1 | 0.1 | 0.35-0.6 | - | 0.15 | 0.1 | 0.15 | Rest |
6005 | 0.6-0.9 | 0.35 | 0.1 | 0.1 | 0.40-0.6 | 0.1 | 0.1 | 0.1 | 0.15 | Rest |
2) Mechanical property
Alloy | Temper | Tensile strength | Yield strength | Elongation |
6063 | T5 | ≥ 160Mpa | ≥ 110Mpa | ≥ 8% |
T6 | ≥ 205Mpa | ≥ 180Mpa | ≥ 8% |
6061 | T6 | ≥ 265Mpa | ≥ 245Mpa | ≥ 8% |
Competitive Advantage:
High difficulty, large size can be accepted.
High-blooded extrudability, we can extrude all kinds of complicated
aluminium alloy radiator.
1).Moderate intensity, it can satisfy various technical requirement
of mechanical working.
2).Suitable physical characteristics, compact internal
organization, well electric conduction and heat conduction
capability.
3).Better capability of accepting anodic oxidation.