Product details
Laser cladding means that the selected coating material is placed
on the surface of the substrate to be coated by different laser
irradiation to be melted simultaneously with a thin layer of the
surface of the substrate, and rapidly solidified to form a very low
dilution. A surface coating that is metallurgically bonded to the
substrate to significantly improve the wear, corrosion, heat,
oxidation and electrical properties of the surface of the substrate
to achieve surface modification or repair, which not only meets the
surface specificity of the material. The performance requirements
save a lot of valuable elements.
| |
| Alloy | Norminal Composition(wt%) | Remark |
| C | Si | Cr | Ni | Mn | Mo | Cu | W | V | Fe |
| 316L | ≤0.03 | ≤1.00 | 16.0-18.0 | 10.0-14.0 | ≤2.00 | 2.0-3.0 | - | - | - | Bal. | |
| 304L | ≤0.03 | ≤1.00 | 18.0-20.0 | 8.0-12.0 | ≤2.00 | - | - | - | - | Bal. | |
| 310S | ≤0.08 | ≤1.50 | 24.0-26.0 | 19.0-22.0 | ≤2.00 | - | - | - | - | Bal. | |
| 17-4PH | ≤0.07 | ≤1.00 | 15.0-17.5 | 3.0~5.0 | ≤1.00 | - | 3.00-5.00 | - | - | Bal. | Nb:0.15-0.45 |
| 15-5PH | ≤0.07 | ≤1.00 | 14.0-15.5 | 3.5~5.5 | ≤1.00 | - | 2.5~4.5 | - | - | Bal. | Nb:0.15-0.45 |
| 4340 | 0.38-0.43 | 0.15-0.35 | 0.7-0.9 | 1.65-2.00 | 0.6-0.8 | 0.2-0.3 | - | - | - | Bal. | |
| S136 | 0.20-0.45 | 0.8-1.0 | 12.0-14.0 | - | ≤1.00 | - | - | - | 0.15-0.40 | Bal. | |
| D2 | 1.40-1.60 | ≤0.4 | 11.0-13.0 | - | ≤0.6 | 0.8-1.2 | - | - | 0.2-0.5 | Bal. | |
| H11 | 0.32-0.45 | 0.6-1 | 4.7-5.2 | - | 0.2-0.5 | 0.8-1.2 | - | - | 0.2-0.6 | Bal. | |
| H13 | 0.32-0.45 | 0.8-1.2 | 4.75-5.5 | - | 0.2-0.5 | 1.1-1.5 | - | - | 0.8-1.2 | Bal. | |
| M2 | 0.78-0.88 | 0.2-0.45 | 3.75-4.5 | - | 0.15-0.4 | 4.5-5.5 | - | 5.5-6.75 | 1.75-2.2 | Bal. | |
| M4 | 1.25-1.40 | 0.2-0.45 | 3.75-4.5 | - | 0.15-0.4 | 4.5-5.5 | - | 5.25-6.5 | 3.75-4.5 | Bal. | |
| T15 | 1.4-1.6 | 0.15-0.4 | 3.75-5.0 | - | 0.15-0.4 | - | - | 11.75-13 | 4.5-5.25 | Bal. | Co:4.75-5.25 |
| 30CrMnSiA | 0.28-0.34 | 0.9-1.2 | 0.8-1.1 | - | 0.8-1.1 | - | - | - | - | Bal. | |
| SAE-1524 | 0.18-0.25 | - | - | - | 1.30-1.65 | - | - | - | - | Bal. | |
| 4605 | 0.4-0.6 | ≤1.00 | - | 1.5-2.5 | - | 0.2-0.5 | - | - | - | Bal. | |
| 8620 | 0.18-0.23 | 0.15-0.35 | 0.4-0.6 | 0.4-0.7 | 0.7-0.9 | 0.15-0.25 | - | - | - | Bal. | |