High Hardness Thermal Spray Powder Coating Wear Resistant
TNOCA02.8043
Description:
high hardness, high temperature resistant, corrosion resistance,
salt fog resistance
Anti-corrosion and salt spray test > 4000hrs
Macro hardness 65 HRC
Maximum temperature 540˚C
Bond strength > 40MPa
Standard: ASTM-C633 ,NEN-EU 5,NEN-ISO 4287,NEN-ISO 4287,ASTM
D2794-93
NEN-ISO 4287,DIN50021-155,TNOCA02.8043
HYDROX AP20 Coating Technical Specifications
List of items | HYDROX AP20 | Standard |
Typical coating composition | Inc625-Cr2O3TiO2 | |
Coating thickness | Bottom ( Inc625) ≥150um | |
| Surface layer ( Cr2O3TiO2) ≥200um | |
Bond strength | > 40MPa | ASTM-C633 |
Maximum temperature | 540˚C | |
Porosity | < 2% | |
Macro hardness | 65 HRC | |
Micro hardness | > 1000HV200 | NEN-EU 5 |
Surface Finish (Ra) | 0.15um-0.4um | NEN-ISO 4287 |
Surface Finish (Rz) | < 4.5um | NEN-ISO 4287 |
Shock Value | > 2J | ASTM D2794-93 |
RPK Material contact area | > 80%,Depth 1,0um | NEN-ISO 4287 |
Anti-corrosion and salt spray test | > 4000hrs | DIN50021-155 |
ECP(Drying) | < -350mV | |
ECP(Semi-dry) | < -350mV | TNOCA02.8043 |
ECP(Wet) | < -350mV | |
To apple ceramic coating on the equipment surface can have
many benefits . Such as high hardness, high temperature resistant,
corrosion resistance, salt fog resistance. Effect is much better
than common electroplating. It works well in ocean industry, food
machinery, water conservancy and hydropower, aerospace and other
industries.