Anodized Surface Sliding Window Aluminium Profiles ISO9001

6063 T5 Custom Anodized Surface Sliding Aluminum Profile Window Aluminium Extrusion

Introduction of Anodized:

1. Hot water flushing: after oxidation, aluminum parts need to be flushed with hot water in order to aging the film. However, the water temperature and time should be strictly controlled. If the water temperature is too high, the film becomes thinner and the color becomes lighter. The above similar problems will also occur if the treatment time is too long. The appropriate temperature and time are: temperature 40 ~ 50 ℃ and time 0.5 ~ 1min.
2. Drying: it is better to dry naturally. Hang the aluminum parts washed with hot water obliquely on the shelf, so that the free water on the working surface flows downward in a vertical direction. The water drops flowing to the lower corner are absorbed with a towel. The color of the film dried by this method is not affected and appears natural.
3. Aging. The aging method can be determined according to the climatic conditions. In summer with strong sunlight, it can be exposed to the sun. In rainy days or winter, it can be baked in an oven. The process conditions are: temperature 40 ~ 50 ℃, time 10 ~ 15min
4. For the repair of unqualified parts, unqualified conductive oxide film parts should be picked out before drying and aging processes. It is difficult to remove the film after drying and aging, which will affect the surface roughness of aluminum parts. For unqualified workpieces, we can take the following simple measures to solve them: first, clamp the unqualified workpieces on the fixture for aluminum anodizing, and then anodize them according to the anodizing method of aluminum in sulfuric acid solution for 2 ~ 3min. After the film is soft and falls off, the conductive anodizing can be carried out again after a little cleaning with alkaline solution and light emitting with nitric acid.

Product Details:

Introduction of Electrophoresis:

Aluminum oxide takes the substrate as the anode and is electrolyzed in the electrolyte to artificially form a protective oxide film on the surface of the substrate. It has strong wear resistance, weather resistance and corrosion resistance.
Aluminum oxide material:
The substrate is used as an anode and placed in the electrolyte for electrolysis. A protective oxide film is artificially formed on the surface of the substrate to form aluminum oxide.
Main features of aluminum oxide material:
1. It has strong wear resistance, weather resistance and corrosion resistance.
2. A variety of colors can be formed on the surface of the substrate to meet your requirements to the greatest extent.
3. Strong hardness, suitable for the production of various construction and industrial materials.

Photos:

Please tell us the information below, and we will give the best suggestion to you !

1. Where you intend to use the aluminium profiles?

2. If you have the estrusion drawing, send us and we develop the correspondence mold.

3. Which color you want or tell us the architectural style you like.

4. Purchase quantity. It will convenient us to give you the best price.