Silane Crosslinkable Xlpe Cable Compound / Polyethylene Compound Linear Type

Browse Categories

Anhui Herrman Machinery Technology Co.,ltd

City: hefei

Province/State:anhui

Country/Region:china

Tel:86-551-65667601

View Contact Details

Silane Crosslinkable Xlpe Cable Compound / Polyethylene Compound Linear Type

Brand Name Herrman
Model Number /
Certification ISO9001:2015,CE,ROSH,SGS
Place of Origin China
Minimum Order Quantity 1000 KGS
Price By Negotiation
Payment Terms L/C, T/T, D/A, D/P,By Negotiation
Supply Ability 15 T per month
Delivery Time 45 working days
Packaging Details By export packing
Product Name Silane crosslinkable in Room Temperature Polyethylene Insulation Compound and Catalyst
Usage Cable making
Material Type Linear type
Permanent deformation after cooling ≤5%
Type and proportion of monomer unit ethylene, 97%
Specific gravity 0.925g/cm3
Shape Pellet
Appearance White
Warranty 1 year
Detailed Product Description

Silane crosslinkable in Room Temperature Polyethylene Insulation Compound and Catalyst Polyethylene Insulation Compound

 

Description

 

Silane crosslinkable in Room Temperature Polyethylene Insulation Compound and Catalyst are used as cable cross linkage material.

 

Feature

 

1 Appearance: White

2 Component content: polyethylene 97%, silane 1 ~ 2%, antioxidant 0.1 ~ 0.5%, other 0.5 ~ 1%

3 Type and proportion of monomer unit: ethylene, 97%

4 Linear type

5 Specific gravity: 0.925 g/cm3

 

Main Specification

 

NO.Testing ItemUnitIndexValue
1

Tensile Strength

 

MPa≥13.523.5
2Elongation at break%≥350730
3

 

Impact brittle temperature

   
 

Test Temperature

 

-76-76
 

Impact embrittlement performance

 

 ≤15/30-0/+30
4

135±2℃×168h]

Air heat ageing

   
 

 

Rate of change of tensile strength

%±20+7
 

 

Rate of change of elongation at break

%±20-6
5

(200℃,0.2 Mpa,15min)

Hot prolongation

   
 

 

Elongation under load

%≤10095
 

 

Permanent deformation after cooling

%≤5

5

 

6Gel content%≥6069
7

Dielectric loss angle tangent

 

 ≤1.0×10-37.1×10-4
8Dielectric constant ≤2.352.32
9

 

20℃ volume resistivity

Ω.m≥1×10144.4×1014
10

 

Dielectric strength

MV/m≥2530

 

​Product Photo

 

 

Product Tags: double sided conductive tape   black conductive tape  
Related Products
Email to this supplier
 
From:
Enter your Email please.
To: Anhui Herrman Machinery Technology Co.,ltd
Subject:
Message:
Characters Remaining: (80/3000)