Chemical Resistant Ptfe Hashima Fusing Machine Belt Customized Size Ptfe Fusing

Browse Categories

Suntex Composite Industrial Co.,Ltd.

City: wuhan

Province/State:hubei

Country/Region:china

Tel:86-027-87879850

Contact Person:
Ms.Fiona Wang View Contact Details

Chemical Resistant Ptfe Hashima Fusing Machine Belt Customized Size Ptfe Fusing

Brand Name	Suntex
Model Number	SL1200
Place of Origin	Jiangsu, China
Minimum Order Quantity	Negotiable
Price	Negotiable
Payment Terms	L/C, D/P, T/T
Supply Ability	300000m/month
Delivery Time	5-20 days
Packaging Details	Fabric rolls packed in cartons loaded on pallets or according to customers' requirements.
Alkali content	Alkali Free
Yarn type	E-Glass
Thickness	1.3mm
Weight	1200g/m2
Width	from 1m to 2m or customized
Weave type	twill woven or plain woven or customized
Coating	two sides vermiculite coated
Color	brown/yellow
Base Material	silica fiberglass cloth
Standing temperature	up to 1000 degree C
Good features	high temperature resistance, good flame retardant ability
Properties	weatherproof, water repellent, good chemical resistance
Application 1	welding and molten metal splash protection, heat and flame shielding
Application 2	chemical plants, oil refineries, ports, and industry fields

Detailed Product Description

Chemical Resistant China Supplier Factory Wholesale Ptfe Hashima Fusing Machine Belt Customized Size Ptfe Fusing

Product Description

High silica fiberglass fabric can be effectively used at steady-state temperatures in 1000 degrees to 1700 degrees without deterioration of the formation of cristobalite structure. The silica fabric has been specially developed to use in the applications to protect an extreme temperature environment. They also have excellent chemical resistance and electrical insulation properties.

BASE FABRIC	Base fabric style No. SL1200
	(Metric)	(English)	Test methods
Weave	12 H Satin	12 H Satin
Yarn
Warp	EC9 136 1*2	ECG 37 1/2
Weft	EC9 136 1*2	ECG 37 1/3
Construction
Warp	19 ± 1 ends/cm	46 ± 2 ends/inch
Weft	14 ± 1 picks/cm	33 ± 2 picks/inch
Weight	1200 ± 30 g/m²	36± 0.9 oz/yd²	ASTM D3776-96
Thickness	1.4 ± 0.08 mm	0.05± 0.003 inch	ASTM D1777-96

COATED FABRIC	Coating style No.VE216-5022
Coating	Coated with vermiculite , two sides
Weight	1250 ± 30 g/m²	36.76 ± 0.88 oz/yd²	ASTM D3776-96
Thickness	1.45 ± 0.05 mm	0.055 ± 0.0019 inch	ASTM D1777-96
Color	brown
Flame resistance	YES		NF 92507
Temp resistance	The maximum working temperature at 1000 ⁰C The peak Temp.(melt point) 1700 ⁰C

product main application
-Insulation jackets, covers, mattress

-Fabric expansion joints

-Fabric ductwork connector

-Fire doors & Fire curtains

-Welding/fire blankets

-Other fire control systems

Product Application

Packaging & Shipping

Product Tags: Ptfe Hashima Fusing Machine Belt Ptfe Fusing Belt Fiberglass Fabric Chemical Resistant Silica Coated Fiberglass

Related Products

Vermiculite Coated Fiberglass Fabric with 750℃ Temperature Resistance and 1070gsm Heavy Weight for Excellent Abrasion Resistance

750℃ Temperature Resistance Vermiculite Coated Fiberglass Cloth with 1070gsm Heavy Weight and Excellent Abrasion Resistance for Welding Blanket

750℃ Temperature Resistance 1070gsm Heavy Weight Vermiculite Coated High Silica Fiberglass Fabric with Excellent Abrasion Resistance for Welding Blankets

High Silica Fiberglass Fabric with Double-Sided Vermiculite Coating for 750℃ Temperature Resistance and Excellent Abrasion Resistance

750℃ Temperature Resistance Vermiculite Coated Fiberglass Fabric with 1070gsm Heavy Weight and Excellent Abrasion Resistance

750℃ Temperature Resistance Vermiculite Coated Silica Fabric with 1070gsm Heavy Weight and Excellent Abrasion Resistance

Email to this supplier


From:	Enter your Email please. Your email is incorrect!
To:	Suntex Composite Industrial Co.,Ltd.
Subject:	Subject is empty!
Message:	Characters Remaining: (80/3000) Please enter 20 to 3000 characters to contact this supplier!