Car Door Cationic Epoxy Edp Paint , Electrophoretic Lacquer Coating No Stratified State

Car Door Cationic Epoxy Edp Paint , Electrophoretic Lacquer Coating No Stratified State

Brand Name HAOLISEN
Model Number HS-6060LB/HS-2668G
Certification IATF16949 , ISO9001
Place of Origin Shanghai China (Mainland)
Minimum Order Quantity Negotiation
Price Negotiation
Supply Ability 200 Tons Per Day
Delivery Time 30-60 Days
Packaging Details 50kg、60 kg、200kg、1000kg packaging barrels
Application field Car doors
Color Grey
Performance Good corrosion resistance
main ingredients Titanium pigment
Cooperation case Xin hong traffic
Detailed Product Description

Solution for the Car doors electrophoresis paint.

 

Product Introduction

 

HS-6060LB/HS-2668G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

 

 

Main ingredients

 

Solvent: alcohol etherAdditives: surface active agent, prevent shrinkage cavity agent
Neutralizing agent: organic acidPigment: carbon black, kaolin, antirust pigment
Curing agent: Fully enclosed multi isocyanateMatrix resin: Acrylic modified epoxy resin

 

Product quality data

 

ProjectTechnical dataTest standard
Resin (HS-6060LB)Gray Paste(HS-2668G)
Appearance——Milky white liquidGray viscous liquid,no agglomerationVisual
pH25℃6.0±1.0——GB/T 9724
Conductivity25℃, μs/cm1400±600——HG/T 3334
Storage stability
No stratified state, and there were no obvious difference compared to before storage
In 5-35 ℃ temperature 1 year

Note: pH, conductivity measurement in the resin/pure water = 1:1 dilution

 

 

Bath on site management project

 

Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:

 

ClassificationProjectControl DataTesting frequency
New bathAnolyte
Electrophoresis tankRatio1:(4-5)-- 
Ripening time24-48-- 
Solid ( 120 ℃ /1h ,% )14±4--once a day
PH5.7-6.22.0-3.5once a day
Conductivity ( μs/cm )1200±4001500±500once a day
P/B0.2-0.3once a week
L panelSmooth horizontal plane and vertical plane without obvious differencesonce a week
Solvent content (%)0.5-1.8once a week
Liquid level Fall head (cm )10-15once a day
ED voltage( V )0-300once a day
Break voltage ( V )≥320once a week
Bath temperature ( ℃ )28-35once a day
ED time( S )60~180once a day
UF - 1 TankSolid content (%)≤2.0once a day
UF - 2 TankSolid content (%)≤0.8once a day
Baking furnaceProvisions furnace temperature( ℃ )180-190once a day
Curing conditionsDrying temperature
(175-185)℃×(20-30)min (With content holding time)
once a day

 

Customer production site

 

Product Tags: cathodic electrocoating   car body coating  