Stone Resistant E Coating Car Body Paint With Anti Rust Pigment Ingredients

Browse Categories

HLS Coatings （Shanghai）Co.Ltd

City: shanghai

Province/State:shanghai

Country/Region:china

Tel:86--13564930110

View Contact Details

Stone Resistant E Coating Car Body Paint With Anti Rust Pigment Ingredients

Brand Name	HAOLISEN
Model Number	HLS-1701ELB/HLS-1701EG
Certification	IATF16949 , ISO9001
Place of Origin	Shanghai China （Mainland）
Minimum Order Quantity	Negotiation
Price	Negotiation
Supply Ability	200 Tons Per Day
Delivery Time	30-60 Days
Packaging Details	50kg、60 kg、200kg、1000kg packaging barrels
Performance	good Resistance to stone
Cooperation case	NBHZCQ
main ingredients	antirust pigment
Application field	Car chassis

Detailed Product Description

Solution for the chassis electrophoresis paint.

Product Introduction :

HLS-1701ELB/HLS-1701EG Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.

This product features shown below:

Coating fullness of good, better substrate hiding	The bath has strong anti-shrinkage and anti-pollution ability.
Ideal for high demand for salt spray industry, such as pipe trench, auto chassis parts, castings.

The main component :

1.Matrix resin: polyurethane modified epoxy resin

2.Curing agent: totally enclosed multi-isocyanates

3.Neutralizing agent: organic acid

Product film performance :

Project		Indicator	Test standard
Appearance	Normal / Abnormal	Normal	Ocular estimate
Hardness	≥	2H	GB/T 6739
Cup drawing	mm,≥	6	GB/T 9753
Adhesion	level	0	GB/T 9286
Flexibility	mm	1	GB/T 1731
Impact	Kg.cm	50	GB/T 1732
Gloss	60°	50-80	GB/T 9754
Water resistance	h,(23±2)℃ ≥	240	GB/T 1733
Acid resistance	h(0.05N H2SO4) ≥	72	GB/T 9274
Alkali resistance	h(0.1N NaOH) ≥	48	GB/T 9274
*Salt spray resistance	film thickness ≥ 20μm	1000	GB/T 1771
Stone strike resistance	level	1.0	DIN55995-1-2001 method

* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.

The production site:

Product Tags: cathodic electrocoating car body coating

Related Products

High Throwing Power E Coating Car Body Paint Does Not Contain Heavy Metal for sale


From:	Enter your Email please. Your email is incorrect!
To:	HLS Coatings （Shanghai）Co.Ltd
Subject:	Subject is empty!
Message:	Characters Remaining: (80/3000) Please enter 20 to 3000 characters to contact this supplier!

Stone Resistant E Coating Car Body Paint With Anti Rust Pigment Ingredients

Stone Resistant E Coating Car Body Paint With Anti Rust Pigment Ingredients

High Throwing Power E Coating Car Body Paint Does Not Contain Heavy Metal

Gray Cationic Epoxy E Coat Paint , Electrolysis Anti Rust Paint For Cars

Anticorrosive E Coating Car Body With Alcohol Ether / Carbon Black Ingredients

Corrosion Resistant Electrodeposition Paint , Pickup Car Body Coating Electrocoat

Flat Appearance E Coating Car Body Paint With Organic Acid / Alcohol Ether Ingredients

Car Door Cationic Epoxy Edp Paint , Electrophoretic Lacquer Coating No Stratified State