Product Application of Polished Rodpolished rod
1. Introduction of polished rod
The polished rods are used to connect sucker rod and pump unite.
2. Manufacturing specification: API 11B
3. Material
3.1. Chemical Composition
The chemical composition of polished rods are any composition of
AISI recommended series steels that conform to chemical and
mechanical property requirements listed below. The chemical and
composition and limits shall be detailed in the material
specification of the manufacturer.
a) Carbon steel:A1SI 1035-10507.
b) Stainless steel: AISI 304/316 or 431 7.
c) Alloy steel:
1) AISI 4120-41407 :
2) AISI 4315-43407
3] AISI 4615-46257
4) AISI 8620- 86307
Chemical composition of polished rod liners shall be as specified
by the manufacturer. Steel polished rod liners shall be sprayed
metal coated.
Chemical analysis shall be performed on each mill heat of steel
used in the manufacture of polished rods. This analysis shall be
performed in accordance with ASTM A751. A material certification is
an acceptable means to conform to this requirement.
3.2. Mechanical Properties for Finished Product
The mechanical properties of polished rods conform to the strength
values as follows:
a) for carbon steels listed in B.3.2,the ultimate tensile strength
shall be in the rang of 90,000 psi to 160,000 psi(621 MPa to 1,103
MPa };
b) for alloy steels listed in B.3.2,the ultimate tensile strength
shall be in the rang of 95,000 psi to 160,000 psi(655 MPa to 1,103
MPa };
c) for stainless steels listed in B.3.2,the minimum ultimate
tensile strength shall be 70,000 psi (482MPa) for 304/316, and
90,000 psi(620 MPa) for 431. ominal value | Rod body diameter D +0.127-0.254(+0.005-0.010)mm(in) | Length Lmm+/- 50mm (Lft +/-2in) | Thread nominal diameter mm(in) | mm (in) Outer thread shoulder outer diameter | Suitable sucker rod size mm (in) | 29 | 28. 6 (11/8) | 2438, 3353, 4877, 6707, 7315, 7925 (8, 11. 16. 22. 24 , 26) | 24 (15/16) PR 27 (1 1/16) PR | | 16 (5/8) 19 (3/4) | 29 | 28. 6 (11/8)rod-upset on one end | 2438, 3353, 4877, 6707 , 7315, 7925 (8. 11, 16. 22 , 24 , 26) | 24 (15/16 ) SR 27 (1 1/16 ) SR | 31.8+0.127-0.254 (1.250+0.005-0.010) 38.1+0.127-0.254
(1.500+0.005-0.010) | | 32 | 31.8(1 1/4) | 3353, 4877, ,6707,7315, 7925 , 9144, 10973 (11, 16, 22 . 24. 26,
30. 36) | 30 (1 3/16 ) PR | | 22(7/8) | 32 | 31.8(1 1/4)rod-upset on one end | 3353, 4877, ,6707,7315, 7925 , 9144, 10973 (11, 16, 22 . 24. 26,
30. 36) | 30 (1 3/16 ) SR | 41.3+0.127-0.254 (1.625+0.005-0.010) | 22(7/8) | 38 | 38. 1 (1 1/2) | 4877, 6707,7315, 7925. 9144. 10973 (16, 22. 24, 26, 30. 36) | 35(1 3/8)PR | | 25(1) | 38 | 38. 1 (1 1/2)rod-upset on one end | 4877, 6707,7315, 7925. 9144. 10973 (16, 22. 24, 26, 30. 36) | 40(1 9/16)SR | 57.2+0.381-0.381 (2.250+0.015-0.015) | 29(1 1/8) |
|