K10 Cemented Tungsten Round Carbide Inserts For MiningTungsten Round Carbide Inserts are mainly made of tungsten carbide
and cobalt powder through metallurgical mixing, crushing, ball
milling, pressing and sintering. The main components of the alloy
are WC and Co, and the contents of WC and Co for different purposes
are different, so they are widely used. It is also called tungsten
carbide plate because of its rectangular plate (or square plate). Technological Process of Tungsten Round Carbide InsertsPowdering → formula according to application requirements → wet
grinding → mixing → pulverizing → crushing → drying → screening →
adding molding agent → re-drying → preparation of mixture after
screening → granulation → molding → pressing → molding → sintering
→ molding (blank) → flaw detection →Packaging →Warehousing Performance characteristics of Tungsten Round Carbide Inserts- Tungsten carbide billets have excellent hardness, high hardness,
good wear resistance, high elastic modulus, high compressive
strength, chemical stability (acid resistance, alkali resistance,
high temperature oxidation resistance), low impact toughness, low
expansion coefficient, heat resistance. good features.
- Tungsten carbide blanks are mainly used to manufacture copper,
aluminum, stainless steel, cold rolled sheet, EI sheet, Q195, SPCC,
silicon steel sheet, hardware, standard parts, high-speed upper and
lower dies, multi-station progressive die punching and other
plates. It is also the first choice for manufacturing high
temperature parts, wear parts, shielding parts and corrosion
resistant parts.
Tungsten Round Carbide Inserts Picture:Round Carbide Inserts Garde & Technical Parameters| Grade | Co% | Hardness
HAR | Density
g/cm | Flexural strength
MPa | Elastic modulus
GPa | Thermal expansion coefficient
10/C | Application | | JX10 | 10 | 91.7 | 14.4 | 4300 | 490 | 5.4 | Copper, aluminum and other thin sheets with thickness less than
0.2mm | | JX15 | 12 | 92.5 | 14.1 | 4500 | 460 | 5.8 | Copper, aluminum, stainless steel, etc | | JX20 | 13 | 90.6 | 14.1 | 4100 | 460 | 5.8 | Strong applicability, copper, aluminum and other thin sheets | | JX35A | 12 | 89.8 | 14.2 | 3400 | 470 | 5.7 | Q195, SPCC and other cold rolled sheets | | JX36 | 15 | 89.4 | 13.8 | 3900 | 430 | 6.3 | EI, SPCC and other cold rolled sheets | | JX40A | 12 | 88.9 | 14.2 | 3300 | 470 | 5.7 | Q195, SPCC and other cold rolled plates, high-speed stamping dies
and multi station progressive dies | | JX45A | 15 | 87.9 | 13.9 | 3200 | 440 | 6.1 | Die for silicon steel sheet, cold rolled sheet, hardware and
standard parts | | JX55 | 20 | 86.4 | 13.5 | 3100 | 390 | 6.8 | Silicon steel sheet, upper and lower punches |
|