Gr2 Titanium Rod ASTM F136
Certification:ISO9001:2015,SGS,TUV
Standard:ASTM B348/AMS4928
Shape: Round bar/hex rod
Application:Medical,industry aerospace
Diameter:≥1.0mm
Length:≤6000mm(normal szie)
Technique: Cold Rolled, hot rolled
Grade:GR5 .Ti6AL-4V. ti6al4v eli.grade 5
Material:Titanium
Surface:Polished
The composition of Grade 5 Titanium Bar is Ti-6Al-4V, which belongs
to (α+β) type Grade 5 Titanium Bar and has good comprehensive
mechanical and mechanical properties. than the strength. Titanium
alloys have low thermal conductivity. The allowable deviation of
the fixed length is +20mm; times The length of the ruler should
also be included in the incision amount of the bar, and the amount
of each incision is 5mm.
| Chemical requirements |
| | N | C | H | Fe | O | Al | V | Pd | Mo | Ni | Ti |
| Gr1 | 0.03 | 0.08 | 0.015 | 0.20 | 0.18 | / | / | / | / | / | bal |
| Gr2 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | / | / | bal |
| Gr5 | 0.05 | 0.08 | 0.015 | 0.40 | 0.20 | 5.5~6.75 | 3.5~4.5 | / | / | / | bal |
| Gr7 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | 0.12~0.25 | / | / | bal |
| Gr12 | 0.03 | 0.08 | 0.015 | 0.30 | 0.25 | / | / | / | 0.2~0.4 | 0.6~0.9 | bal |
| Tensile requirements |
| Grade | Tensile srength(min) | Yeild strength(mm) | Elongation(%) |
| | KSI | MPa | Ksi | MPa | |
| 1 | 35 | 240 | 20 | 138 | 24 |
| 2 | 50 | 345 | 40 | 275 | 20 |
| 5 | 130 | 895 | 120 | 828 | 10 |
| 7 | 50 | 345 | 40 | 275 | 20 |
| 12 | 70 | 438 | 50 | 345 | 18 |
| Item Name | Titanium bar/titanium rod |
| Standard | ASTM B348,ASTM F67,ASTM F136, AMS 4928 |
| Material | Gr1 Gr2 Gr3 Gr4 Gr5 |
| Diameter | 0.8~500mm |
| Length | 500~6000mm or according to customers' request |
| Product Status | Cold rolled(Y)~Hot rolled(R)~Annealed (M)~Solid Status |
| Shape | Round bar, square bar , hex bar |
| Feature | 1.Polished surface without any defects free from cracks no pittings
2.Two ends flating making sure length torlerance and good looking |
| Certificate | ISO9001:2015, TUV, material test certificate acc EN10204.3.1 |