CuBe2Pb C17300 Copper Alloy Rod 1.6mmx3000mm By ASTM B196

CUBERYLLIUM® Copper Alloy C17300(CuBe2Pb) Rod 1.6mmx3000mm By ASTM B196

Product Description:

Name: CUBERYLLIUM® Copper Alloy Rod

Grade: C17300(CuBe2Pb)

End Product Form: Rods/ Bars

Standard: ASTM B196

State of product: TD04

Processing: Seamless / Welding

Feature: With high strength and high conductivity

Package: Pack in coil+waterproofing winding film+Drier+Wooden Case

Specification: Dia 1.6mm; Length 3000mm or according customers' requirement

CUBERYLLIUM®  maintains an inventory of beryllium copper alloys, including beryllium copper strips, beryllium copper rods/bars, beryllium copper wires and so on.

The small ratio of beryllium to copper creates a family of high-copper alloys with strength as high as alloy steel. The commercial grades of beryllium copper alloys contain from 0.4 to 2.0% berylliium. The two families consist of high strength with moderate conductivity copper alloy C17200 and C17300, high conductivity with moderate strength copper alloy C17500 and C17510. The principal characteristics of these alloys are their excellent response to precipitation-hardening treatments, excellent thermal conductivity, and resistance to stress relaxation.

Chemical Composition of CuBe2Pb / C17300 (CDA 173) Beryllium Copper Alloys:

Note: Copper plus additions equal 99.5% minimum.

Typical Physical Properties of CuBe2Pb / C17300 (CDA 173) Beryllium Copper Alloys:

Density: 8.36g/cm3

Density before age hardening: 8.25g/cm3

Melting Range: 870~980℃

Elastic Modulus((kg/mm2 (103)): 13.4

Thermal Expansion Coefficient(20 °C to 200 °C m/m/°C): 17 x 10 -6

Thermal Conductivity(cal/(cm-s-°C)): 0.25

Mechanical and Electrical Properties of CuBe2Pb / C17300 (CDA 173) Beryllium Rods:

Product Photo:

Benefits of CuBe2Pb / C17300 (CDA173) Beryllium Copper Alloys:

• High stiffness for insertion applications
• Excellent in for anti-galling concerns
• Excellent machinability
• Good electrical and thermal conductivity
• Low friction properties
• Excellent corrosion and erosion resistance
• Non-magnetic

Key Technology of Beryllium Copper(Heat treatment)

Age Hardening

Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.

FAQ:

Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?

A1: 1: The Biggest Coil weight could be reach 1200kg/Coil.

2:We are the only one who melting by Vacuum semi-Continuous Furnace.

3:Surface further polishing for top clients.

Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid before the delivery.

Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation, Grain Refinement

Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the amount is different.