DIN 603 Steel Nut Bolts

Browse Categories

Jiaxing City Qunbang Hardware Co., Ltd

City: jiaxing

Province/State:zhejiang

Country/Region:china

Tel:86-573-82071082

Contact Person:
Mr.Lance View Contact Details

DIN 603 Steel Nut Bolts

Brand Name	QBH
Model Number	DIN603
Certification	ISO9001
Place of Origin	CHINA
Minimum Order Quantity	900kg
Price	Negotiation
Payment Terms	L/C, T/T
Supply Ability	500TON/MONTH
Delivery Time	30DAYS
Packaging Details	25KG/CTN,36CTN/PALLET or small packing
Standard	DIN603
Material	Carbon Steel
Size	M5-M20
Finish	ZP YZP HDG BLACK
Grade	4.8 6.8 8.8-12.8ect
Packing	Carton and pallet or according to the customer's requirement
Sample	Free Sample
Thread	Mushroom head square neck
Lead time	Per on order quantity
Type	Hexagon Head
Advantage	we can manufacture according to client design,OEM / ODM / customized service provided
Oem	yes,welcome

Detailed Product Description

DIN 603 Cup Head Square Neck Bolt

Specification

DIN 603 - Mushroom head square neck bolts

Current norm: DIN 603
Equivalent norms: ISO 8677; CSN 021319; PN 82406; UNI 5731

Legend:

b - length of the thread (at least)
l - length of bolt
d - the nominal diameter of the thread
k - head height
ds - diameter of the screw shank
dk - head diameter
f - height squared
v - width of the square
r1 - Head radius
lg - length of the shank to thread
ls - length of the shank to the start of the thread

Makings:QBH

Steel: 4.6,8.8
Stainless: A2, A4
Plastic: -
Non Ferrous: -
Thread: 6g

Table according to DIN 603:

Thread d		M5	M6	M8	M10	M12	M16	M20
P		0,8	1	1,25	1,5	1,75	2	2,5
b	l < 125mm	16	18	22	26	30	38	46
	125 < l < 200mm	22	24	28	32	36	44	52
	l > 200mm	-	-	41	45	49	57	65
dk	max.	13,55	16,55	20,65	24,65	30,65	38,8	46,8
dk	min.	12,45	15,45	19,35	23,35	29,35	37,2	45,2
ds	max.	5	6	8	10	12	16	20
ds	min.	4,52	5,52	7,42	9,42	11,3	15,3	19,16
f	max.	4,1	4,6	5,6	6,6	8,75	12,9	15,9
f	min.	2,9	3,4	4,4	5,4	7,25	11,1	14,1
k	max.	3,3	3,88	4,88	5,38	6,95	8,95	11,05
k	min.	2,7	3,12	4,12	4,62	6,05	8,05	9,95
r1	approx.	10,7	12,6	16	19,2	24,1	29,3	33,9
r2	max.	0,5	0,5	0,5	0,5	1	1	1
r3	max.	0,75	0,9	1,2	1,5	1,8	2,4	3
v	max.	5,48	6,48	8,58	10,58	12,7	16,7	20,84
v	min.	4,52	5,52	7,42	9,42	11,3	15,3	19,16

Tab2

l			M5		M6		M8		M10		M12		M16		M20
nominal size	min.	max.	ls min.	lg max.	ls min.	lg max.	ls min.	lg max.	ls min.	lg max.	ls min.	lg max.	ls min.	lg max.	ls min.	lg max.
16	15,1	16,9	-	8	-	10
20	18,95	21,05	-	8	-	10	-	12	-	14
25	23,95	26,05	-	8	-	10	-	12	-	14
30	28,95	31,05	-	18	-	10	-	12	-	14	-	18
35	33,75	36,25	15	19	12	17	-	12	-	14	-	18
40	38,75	41,25	20	24	17	22	11,75	18	-	14	-	18
45	43,75	46,25	25	29	22	27	16,75	23	11,5	19	-	18
50	48,75	51,25	30	34	27	32	21,75	28	16,5	24	-	18
55	53,5	56,5	35	39	32	37	26,75	33	21,5	29	16,25	25	-	23
60	58,5	61,5	40	44	37	42	31,75	38	26,5	34	21,25	30	-	23
65	63,5	66,5	45	49	42	47	36,75	43	31,5	39	26,75	35	17	27
70	68,5	71,5	50	54	47	52	41,75	48	36,5	44	31,25	40	22	32	-	28,5
80	78,5	81,5	60	64	57	62	51,75	58	46,5	54	41,25	50	32	42	21,5	34
90	88,25	91,75			67	72	61,75	68	56,5	64	51,25	60	42	52	31,5	44
100	98,25	101,75			77	82	71,75	78	66,5	74	61,25	70	52	62	41,5	54
110	108,25	111,75			87	92	81,75	88	76,5	84	71,25	80	62	72	51,5	64
120	118,25	121,75			97	102	91,75	98	86,5	94	81,25	90	72	82	61,5	74
130	128	132			101	106	95,75	102	90,5	98	85,25	94	76	86	65,5	78
140	138	142			111	116	105,75	112	108,5	108	95,25	104	86	96	75,5	8
150	148	152			121	126	115,75	122	110,5	118	105,25	114	96	106	85,5	98
160	156	164							120,5	128	115,25	124	106	116	95,5	108
180	176	184							140,5	148	135,25	144	126	136	115,5	128
200	195,4	204,6							160,5	168	155,25	164	146	156	135,5	148

Process flow

Cold forging

Annealing treatment(if need) ➨ wiredrawing ➨ clod forging ➨ thread rolling ➨make heat treatment(if need) ➨ Finish ➨ Packing

Hot forging

Cutting material ➨ hot forging ➨ turning ➨ shrink diameter(half thread) ➨thread rolling ➨ make heat treatment(if need) ➨ Finish ➨ Packing

Product Grade

Class4.8 Class5.8 Class6.8 Class8.8 Class10.9 Class12.9

NO.	Mechanical or physical property		Property class
			4.6	4.8	5.6	5.8	6.8	8.8		9.8	10.9	12.9/12.9
			4.6	4.8	5.6	5.8	6.8	D≤16mm^a	d＞16mm^b	d≤16mm	10.9	12.9/12.9
1	Tensile strength R_m,Mpa	nom.^c	400		500		600	800		900	1000	1200
1	Tensile strength R_m,Mpa	max.	400	420	500	520	600	800	830	900	1040	1220
2	Lower yield strength R_eL,Mpa	nom.^c	240	——	300	——	——	——	——	——	——	——
2	Lower yield strength R_eL,Mpa	max.	240	——	300	——	——	——	——	——	——	——
3	Stress at 0,2 % nonproportional elongation R_p0.2,Mpa	nom.^c	——	——	——	——	——	640	640	720	900	1080
3	Stress at 0,2 % nonproportional elongation R_p0.2,Mpa	max.	——	——	——	——	——	640	660	720	940	1100
4	Stress at 0,0048 d non-proportional elongation for full-size fasteners R_p^f,Mpa	nom.^c	——	320	——	400	480	——	——	——	——	——
4		max.	——	340^e	——	420^e	480^e	——	——	——	——	——
5	Stress under proof load S_p^f,Mpa	nom.	225	310	280	380	440	580	600	650	830	970
5	Proof S_p,nom/R_{eL min} Or strength S_p,nom/R_p0.2min Or rati S_p,nom/R_{pf min}		0.94	0.91	0.93	0.9	0.92	0.91	0.91	0.9	0.88	0.88
6	Percentage elongation after fracture for machined test pieces,A,%	min.	22	-—	20	——	——	12	12	10	9	8
7	Percentage reduction of area after fracture for machined test pieces,Z,%	min.	——					52		48	48	44
8	Elongation after fracture for full-size fasteners,A_f	min.	——	0.24	——	0.22	0.2	——	——	——	——	——
9	Head soundness		No fracture
10	Vickers hardness, HV, F≥98N	min.	120	130	155	160	190	250	255	290	320	385
10	Vickers hardness, HV, F≥98N	max.	220^g				250	320	335	360	380	435
11	Brinell hardness, HBW ,F=30D²	min.	114	124	147	152	181	238	242	276	304	366
11	Brinell hardness, HBW ,F=30D²	max.	209^g				238	304	318	342	361	414
12	Rockwell hardness,HRB , HRB	min.	67	71	79	82	89
	Rockwell hardness,HRB , HRB	max.	95^g				99.5
	Rockwell hardness, HRC	min.	——					22	23	28	32	39
	Rockwell hardness, HRC	max.	——					32	34	37	39	44
13	Surface hardness HV 0.3	max.	——					h			h,j	h,j
14	Height of non-decarburized thread zone,E,mm	min.	——					1/2H₁			2/3H₁	3/4H₁
14	Depth of complete decarburization in the thread,G,mm	max.	——					0.015
15	Reduction of hardness after retempering,HV	max.	——					20
16	Breaking torque, M_B,N·m	min.	——					in accordance with ISO 898-7
17	Impact strength, K_V^K,I,J	min.	——		27	——		27	27	27	27	m
18	Surface integrity in accordance with		ISO 6157-1ⁿ									ISO 6157-3
a Values do not apply for structural bolting. b For structural bolting d W M12. c Nominal values are specified only for the purpose of the designation system for property classes.See Clause 5. d In cases where the lower yield strength ReL cannot be determined, it is permissible to measure the stress at 0,2 % non-proportional elongation Rp0,2. e For the property classes 4.8, 5.8 and 6.8 the values for Rpf min are under investigation. The present values are given for calculation of the proof stress ratio only. They are not test values. f Proof loads are specified in Tables 5 and 7. g Hardness determined at the end of a fastener shall be 250 HV, 238 HB or 99,5 HRB maximum. h Surface hardness shall not be more than 30 Vickers points above the measured core hardness of the fastener when determination of both surface hardness and core hardness are carried out with HV 0,3. i Any increase in hardness at the surface which indicates that the surface hardness exceeds 390 HV is not acceptable. j Any increase in hardness at the surface which indicates that the surface hardness exceeds 435 HV is not acceptable. k Values are determined at a test temperature of −20 °C, see 9.14. l Applies to d W 16 mm. m Value for KV is under investigation. n Instead of ISO 6157-1, ISO 6157-3 may apply by agreement between the manufacturer and the purchaser.

Materials and Chemical compstition

1008

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu	Al
0.06	0.06	0.33	0.013	0.003	0.01	0	0.01	0.028

1035

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu
0.34	0.13	0.73	0.012	0.002	0.02	0.01	0.02

10B21

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	B
0.2	0.04	0.81	0.017	0.007	0.017	0.0021

1045

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu
0.45	0.23	0.58	0.014	0.006	0.057	0.008	0.016

40CR

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu
0.4	0.21	0.54	0.015	0.008	0.95	0.02	0.02

35CRMO

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu	Mo
0.35	0.22	0.59	0.01	0.003	0.93	0.01	0.01	0.21

42CRMO

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu	Mo
0.42	0.27	0.92	0.013	0.004	1.01	0.03	0.04	0.2

Finish

PLAIN ZP YZP BLACK HDG DACROMET GEOMET CHROME NICKEL AND SO ON

PACKING

QBH BULK

20-25KG/CTN,36CTNS/PALLET

20-30KG/BAGS,36BAGS/PALLET

ONE TON/BOXES

50KG/ IRON DRUM,12 IRON DRUMS/PALLET

QBH SMALL PACKING

Packing in small boxes according to customer’s requirements

Packing in plastic bag according to customer’s requirements

QBH PALLET TYPE

SOLID WOOD FUMIGATION PALLET

EURO Pallet

THREE SPLINT PALLET

WOODEN BOX

The advantages of QBH

QBH brand sales to the main quality assurance.
Years of export trade management, excellent service, word-of-mouth guarantee.
By working with TUV,escort for quality.
Customization of non-standard parts can be made according to customer's requirements and drawings.
For quality customers,we can provide a certain credit period.

Product Tags: 6.8 Steel Nut Bolts DIN 603 Steel Nut Bolts DIN 603 Cup Head Square Neck Bolt

Related Products

DIN605 Long Square Flat Countersunk Head Square Neck Bolts for sale


From:	Enter your Email please. Your email is incorrect!
To:	Jiaxing City Qunbang Hardware Co., Ltd
Subject:	Subject is empty!
Message:	Characters Remaining: (80/3000) Please enter 20 to 3000 characters to contact this supplier!

DIN 603 Steel Nut Bolts

DIN 603 Steel Nut Bolts

Legend:

Makings:QBH

Table according to DIN 603:

DIN605 Long Square Flat Countersunk Head Square Neck Bolts

Ifi 544 Hardware Metric Round Head Ribbed Neck Bolts 304 316 Stainless Steel

DIN188 Double Nib T-Head Bolts In 304/316 Stainless Steel For OEM Needs

M2-M36 DIN917 Low Type Hexagon Cap Nuts Perfect Choice For Build

All Thread DIN15237 Flat Head Elevator Screw Bolt Free Sample

DIN15237 All Thread Elevator Bolt Stainless Steel 304 316