10.9 HDG YZP BLACK ZP M6 TO M20 Carbon Steel Bolt

Brand Name	QBH
Model Number	M6-M20
Certification	ISO9001
Place of Origin	CHINA
Minimum Order Quantity	900KG
Price	Negotiation
Payment Terms	L/C, T/T,OA
Supply Ability	600TON/MONTH
Delivery Time	30DAYS
Packaging Details	25KG/CTN,36CTN/PALLET or small packing
SIZE	M6-M20
LENGTH	ALL KIND OF LENGTH
Material	Carbon steel
samples	free samples
surface	HDG YZP ZP BLACK

Detailed Product Description

Socket head cap screws are commonly used in machine assembly for removable panels and parts. They have a round cap with a hex head and are tightened with a socket wrench drive. Longer caps are easier to see when fastened, while button and flat head caps are less likely to snag clothing or linkages. Cap screws with a black oxide or armor coat finish resist corrosion.

Product Grade

Class4.8 Class5.8 Class6.8 Class8.8 Class10.9 Class12.9

Mechanical property

NO.	Mechanical or physical property		Property class
			4.6	4.8	5.6	5.8	6.8	8.8		9.8	10.9	12.9/12.9
			4.6	4.8	5.6	5.8	6.8	D≤16mm^a	d＞16mm^b	d≤16mm	10.9	12.9/12.9
1	Tensile strength R_m,Mpa	nom.^c	400		500		600	800		900	1000	1200
1	Tensile strength R_m,Mpa	max.	400	420	500	520	600	800	830	900	1040	1220
2	Lower yield strength R_eL,Mpa	nom.^c	240	——	300	——	——	——	——	——	——	——
2	Lower yield strength R_eL,Mpa	max.	240	——	300	——	——	——	——	——	——	——
3	Stress at 0,2 % nonproportional elongation R_p0.2,Mpa	nom.^c	——	——	——	——	——	640	640	720	900	1080
3	Stress at 0,2 % nonproportional elongation R_p0.2,Mpa	max.	——	——	——	——	——	640	660	720	940	1100
4	Stress at 0,0048 d non-proportional elongation for full-size fasteners R_p^f,Mpa	nom.^c	——	320	——	400	480	——	——	——	——	——
4		max.	——	340^e	——	420^e	480^e	——	——	——	——	——
5	Stress under proof load S_p^f,Mpa	nom.	225	310	280	380	440	580	600	650	830	970
5	Proof S_p,nom/R_{eL min} Or strength S_p,nom/R_p0.2min Or rati S_p,nom/R_{pf min}		0.94	0.91	0.93	0.9	0.92	0.91	0.91	0.9	0.88	0.88
6	Percentage elongation after fracture for machined test pieces,A,%	min.	22	-—	20	——	——	12	12	10	9	8
7	Percentage reduction of area after fracture for machined test pieces,Z,%	min.	——					52		48	48	44
8	Elongation after fracture for full-size fasteners,A_f	min.	——	0.24	——	0.22	0.2	——	——	——	——	——
9	Head soundness		No fracture
10	Vickers hardness, HV, F≥98N	min.	120	130	155	160	190	250	255	290	320	385
10	Vickers hardness, HV, F≥98N	max.	220^g				250	320	335	360	380	435
11	Brinell hardness, HBW ,F=30D²	min.	114	124	147	152	181	238	242	276	304	366
11	Brinell hardness, HBW ,F=30D²	max.	209^g				238	304	318	342	361	414
12	Rockwell hardness,HRB , HRB	min.	67	71	79	82	89
	Rockwell hardness,HRB , HRB	max.	95^g				99.5
	Rockwell hardness, HRC	min.	——					22	23	28	32	39
	Rockwell hardness, HRC	max.	——					32	34	37	39	44
13	Surface hardness HV 0.3	max.	——					h			h,j	h,j
14	Height of non-decarburized thread zone,E,mm	min.	——					1/2H₁			2/3H₁	3/4H₁
14	Depth of complete decarburization in the thread,G,mm	max.	——					0.015
15	Reduction of hardness after retempering,HV	max.	——					20
16	Breaking torque, M_B,N·m	min.	——					in accordance with ISO 898-7
17	Impact strength, K_V^K,I,J	min.	——		27	——		27	27	27	27	m
18	Surface integrity in accordance with		ISO 6157-1ⁿ									ISO 6157-3
a Values do not apply for structural bolting. b For structural bolting d W M12. c Nominal values are specified only for the purpose of the designation system for property classes.See Clause 5. d In cases where the lower yield strength ReL cannot be determined, it is permissible to measure the stress at 0,2 % non-proportional elongation Rp0,2. e For the property classes 4.8, 5.8 and 6.8 the values for Rpf min are under investigation. The present values are given for calculation of the proof stress ratio only. They are not test values. f Proof loads are specified in Tables 5 and 7. g Hardness determined at the end of a fastener shall be 250 HV, 238 HB or 99,5 HRB maximum. h Surface hardness shall not be more than 30 Vickers points above the measured core hardness of the fastener when determination of both surface hardness and core hardness are carried out with HV 0,3. i Any increase in hardness at the surface which indicates that the surface hardness exceeds 390 HV is not acceptable. j Any increase in hardness at the surface which indicates that the surface hardness exceeds 435 HV is not acceptable. k Values are determined at a test temperature of −20 °C, see 9.14. l Applies to d W 16 mm. m Value for KV is under investigation. n Instead of ISO 6157-1, ISO 6157-3 may apply by agreement between the manufacturer and the purchaser.

Materials and Chemical compstition

1008

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu	Al
0.06	0.06	0.33	0.013	0.003	0.01	0	0.01	0.028

1035

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu
0.34	0.13	0.73	0.012	0.002	0.02	0.01	0.02

10B21

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	B
0.2	0.04	0.81	0.017	0.007	0.017	0.0021

1045

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu
0.45	0.23	0.58	0.014	0.006	0.057	0.008	0.016

40CR

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu
0.4	0.21	0.54	0.015	0.008	0.95	0.02	0.02

35CRMO

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu	Mo
0.35	0.22	0.59	0.01	0.003	0.93	0.01	0.01	0.21

42CRMO

CHEMICAL COMPOSI %
C	Si	Mn	P	S	Cr	Ni	Cu	Mo
0.42	0.27	0.92	0.013	0.004	1.01	0.03	0.04	0.2

Finish

PLAIN ZP YZP BLACK HDG DACROMET GEOMET CHROME NICKEL AND SO ON

PACKING

QBH BULK

20-25KG/CTN,36CTNS/PALLET

20-30KG/BAGS,36BAGS/PALLET

ONE TON/BOXES

50KG/ IRON DRUM,12 IRON DRUMS/PALLET

QBH SMALL PACKING

Packing in small boxes according to customer’s requirements

Packing in plastic bag according to customer’s requirements

QBH PALLET TYPE

SOLID WOOD FUMIGATION PALLET

EURO Pallet

THREE SPLINT PALLET

WOODEN BOX

The advantages of QBH

QBH brand sales to the main quality assurance.
Years of export trade management, excellent service, word-of-mouth guarantee.
By working with TUV,escort for quality.
Customization of non-standard parts can be made according to customer's requirements and drawings.
For quality customers,we can provide a certain credit period.

Product Tags: 10.9 Carbon Steel Bolt M20 Carbon Steel Bolt 4.8 Hexagonal Socket Head Cap Screw

Related Products

ASTM A325 A325m HDG Carbon Stainless Steel Full Half Thread 2h Nut F436m Washer Building Material Anchor Structural Bolt

High Strength Screws External Black Hexagon Bolts Grade 12.9 M6-M30

Copper Plated Welding M3 Stainless Steel Hex Head Bolts Din hex flange bolt

QBH 1/4-1-1/2 IFI 115 Carbon Steel/Stainless Steel 12 Point Screws IFI115 Flange Spline Bolts

QBH ZP HDG Black Hex Serrated Flange Head Self-Tapping Concrete Screw Anchor

QBH Black Green WZP YZP Yellow White Zinc Plated Trumpet Head Double Or Single Threaded Carbon Steel Drywall Screws

Email to this supplier


From:	Enter your Email please. Your email is incorrect!
To:	Jiaxing City Qunbang Hardware Co., Ltd
Subject:	Subject is empty!
Message:	Characters Remaining: (80/3000) Please enter 20 to 3000 characters to contact this supplier!