IH899 is double-stretched Polyimide film as coated acrylic
pressure-sensitive adhesive. Which has low viscosity and good high
temperature resistance. And covered with blue release film for easy
die-cutting and forming.
Low adhesion, excellent heat resistance performance and ROHS
compliance make these protective films ideal for surface protection
of flat materials such as FPC during high-temperature processing or
as temporary coverings.
Test Item | Test Value | Test Method |
Backing thickness(mm) | 0.025±0.003 | Micrometer |
Total thickness(mm) (Without Release liner) | 0.042+0.003/-0.002 | Micrometer |
Color | Amber | / |
Peeling Strength (gf/25mm) | 40-70 | GBT 2792-2014 |
三180 (High temperature climb peel force) | GBT 2792-2014 |
Maximum use temperature (C) | 200C | Using condition :200C /2H for steel plate &FPC ,no residue and
no wrinkle after cooling |
Storage Conditions, Temperature Range & Humidity Range For
optimal conditions for storage: 10-30C and relative humidity 40-70%
with direct sunlight avoided at times (above 40C & 75%RH), 6
months storage duration with recommended precautions as set out
above; be kept away from heat sources such as fireplaces &
radiators etc
Ling: To maintain optimal conditions, objects should have surfaces
which are clean, dry, and free from oil or any other source of
pollution;
Ling In order for pressure-sensitive adhesives to adhere correctly,
sufficient pressure must be applied when pressing; otherwise it
could have detrimental effects on the characteristics and
aesthetics of the final product.
Ling cannot be used outdoors due to exposure to outdoor weather and
may leave adhesive residue when removed from its substrate surface.
Notes:The data listed is measured against laboratory standards;
actual user usage conditions and methods could alter these
measurements significantly, so it is recommended to test any
product before use.