2mm thickness Astm Aisi 409l 410 420 430 440c Stainless steel coil for handrails

Prepainted Corrugated Galvanized Steel Sheet For Sale. Manufacturers & Suppliers. Quote!

201
201 stainless steel, with a certain acid resistance, alkali resistance, high density, polishing without bubbles, no pinhole and other characteristics, is the production of all kinds of watchcase, watchband cover high quality materials.Mainly used for decorative pipe, industrial pipe, some shallow stretching products.

(C)≤0.15
(Si)≤1.00
(Mn)5.5～7.50
(Cr)16.0～18.0
(N)≤0.25
(P)≤0.060
(S)≤0.030
(Ni)3.5-5.5

304
304 stainless steel is a common material in stainless steel with a density of 7.93 g/cm, also known in the industry as 18/8 stainless steel.High temperature resistance 800℃, with the characteristics of good processing performance, high toughness, widely used in the industrial and furniture decoration industry and food and medical industry.
Tensile strength b (MPa)≥515-1035
304 stainless steel atlas
304 stainless steel atlas (6 sheets)
The yield strength is 0.2 (MPa)≥205
Elongation = 5 (%)≥40
Reduction of area bits of p (%)?
Hardness: 201 HBW or less;
92 HRB or less;
210 hv or less
Density (20℃, g/cm) : 7.93
Melting point (℃) : 1398~1454
Specific heat capacity (0~100℃, KJ· kg-1k-1) : 0.50
Thermal conductivity (W·m-1· k-1) :(100℃) 16.3, (500℃) 21.5
Linear expansion coefficient (10-6· k-1) :(0~100℃) 17.2, (0~500℃) 18.4
Resistivity (20 ℃, 10-6 Ω m2 / m) : 0.73
Longitudinal modulus of elasticity (20℃, KN/mm2) : 193

316
316 stainless steel, 18cr-12ni-2.5 Mo due to the addition of Mo, so its corrosion resistance, atmospheric corrosion resistance and high temperature strength is particularly good, can be used in harsh conditions;
Excellent work hardening (non-magnetic).
Equipment for the production of seawater, chemicals, dyes, papermaking, oxalic acid and fertilizers;
Photography, food industry, coastal facilities, ropes, CD rods, bolts, nuts.
Chemical composition of 316 stainless steel: C≤0.08, Si≤1.00, Mn≤2.00, P≤0.045, S≤0.03, Ni:10.0-14.0, Cr:16.0-18.5, Mo:2.0-3.0.
Mechanical properties of 316 stainless steel, tensile strength (Mpa) 620 MIN, yield strength (Mpa) 310 MIN, elongation (%) 30 MIN, area reduction (%) 40 MIN, density of 316 stainless steel 8.03g /cm3, austenitic stainless steel is generally used this value.

316L
316L is widely used in the chemical industry due to its excellent corrosion resistance. 316L is also a derivative of 18-8 austenitic stainless steel, with 2 ~ 3% Mo element added.
On the basis of 316L, many kinds of steel are also derived, such as 316Ti after adding a small amount of Ti, 316N after adding a small amount of N, and 317L after increasing the content of Ni and Mo.
C :≤0.030
Si: ≤1.00
Mn:≤2.00
S : ≤0.030
P : ≤0.045
Cr:16.00～18.00
Ni:10.00～14.00
Mo:2.00～3.00

316ti
316TI, a metallic material, is added to SUS316 steel to improve its resistance to intergranular corrosion.Used to resist sulfuric acid, phosphoric acid, acetic acid, acetic acid equipment.
C:≤0.08
Si≤1.00
Mn≤2.00
P≤0.035
S≤0.030
Ni 11.00~14.00
Cr 16.00~19.00
Mo 1.80~2.50

410
Stainless steel 410 is produced according to American ASTM standard, equivalent to China's 1Cr13 stainless steel, S41000 (American AISI, ASTM).Carbon 0.15%, chrome 13%,410 stainless steel: good corrosion resistance, machinability, general purpose blade class, valve class.Heat treatment of 410 stainless steel: solid solution treatment (℃) 800-900 slow cooling or 750 fast cooling.Chemical composition of 410 stainless steel: C≤0.15,Si≤1.00,Mn≤1.00,P≤0.035,S≤0.030,Cr=11.50~13.50.
416
416 stainless steel is a kind of steel with good cutting performance in stainless steel. 416 stainless steel is mainly used in the production of solenoid valves, micro-special motors and electrical components.The above materials are free cutting stainless steel, especially suitable for automatic lathes, CNC lathes mass production.
C: 0.15 or lessMn: 1.25 or lessSi: 1.00 or lessCr: 12.0 ~ 14.0Ni: less than or equal to 0.60% nickel is allowedP: 0.06 or lessS: 0.15 or higherMo: molybdenum less than or equal to 0.60% can be added

Chemical composition and mechanical properties of stainless steel