80 Microns Polymer Hot Melt Adhesive Film For PP Building Material Metal Composite Panel

Grade:PP008

Product:80 Microns Polymer Adhesive Film for PP Building Material-Metal Composite Panel

Decriptions

The polymer adhesive film is a maleic anhydride functionalized polymer mixture hot melt adhesive film,developed from years of theoretical and application experience in the field of hot melt adhesive film.

PP008 polymer adhesive film is made by multi-layer co-extrusion blowing equipment, suitable for the composite of PP and metal materials.The film is three layer and double side with adhesive resins, one side is PE hot melt adhesive resin and another side is PP hot melt adhesive resin.The processing technology of the product is mild, and the hollow PP and honeycomb PP will not be deformed or damaged during the compounding process, meanwhile it has excellent peel strength of bonding aluminum and galvanized. The bonding effect of tinplate and other materials is excellent, and it is an ideal material for the bonding of pp composite building materials.

Application

PP008 adhesive film is used for PP material - metal panels, such as PP hollow-aluminium panel and PP honeycomb-aluminium panel and PP honeycomb- metal panel etc.

Advantages

Excellent bonding strength

Processing temperature is moderation and keep the PP materials performance well without damage or deformation

Low costs and environmental protection and no formaldehyde

Physical Properties

♦These are typical properties and not intended as specification

Specifications:

Width: 50mm-1600mm (Customization available)

Length: 1500m/ roll or customization

Processing Suggestions :

Adhesive Layer Structure: PP materials+PP008 film+metal sheet

Bonding Temperature: 170℃-190℃

Bonding Press Force: > 7.5 kg/cm2

QC Standard: IS09001:2015

Packing and Storage:

12 Rolls/Pallet,60- 80 KG/Roll (Customization available)；

Keep in a dry cool place. Avoid direct sunlight, ventilation, and moisture. The storage period at room temperature is 12 months. If the film color changes and elongation is found to decrease by 50%, do not use it.

Remarks: The above information and technical data are based on our existing product knowledge and experience. We do not guarantee the above content and do not assume legal responsibility. Customers must do a sample test before using our products to ensure the best processing conditions.