Factory Wholesale Price Brass Tee Branch Pneumatic Parts Reducing
Tee Copper
The UNS C70600 Reducer helps to reduce the flow rate in various equipment, especially
where the use of seawater is involved. They are used in
shipbuilding industries as the CuNi 90/10 End Cap shows good resistance in the seawater environment. This includes
resistance to pitting and stress corrosion cracking, along with
high resistance to crevice corrosion. The CW352h Saddle is also well-known for its properties which include high
weldability, fabricability, and they resist biofouling too. The CuNi 90/10 Concentric Reducers show good resistance in high temperature situations and hence they
can be found in condensers and heat exchangers.
While explaining what is Copper Nickel 90/10 Fittings, it is essential to know where they are used. The UNS C70600 Fittings are basically fittings made of 90% copper and 10% nickel alloy. It
also contains a trace amount of other materials such as manganese
and iron in its chemical composition. The content of the alloy in
the 90/10 Copper Nickel Pipe Fittings help it to gain enhanced strength and better corrosion resistance.
Manufacturers offer the Copper Nickel 90/10 Tee and other products according to the specified requirements of the
clients. Their shape, size, dimensions, and surface finishes can be
customized as per the application.
Clients should buy 9010 Copper Nickel Equal Tee from experienced manufacturers, who use expert professionals and
advanced technology in the production process. This would help to
enhance the quality of the ASTM B466 UNS C70600 Reducing Tee and have products with enhanced lifespan. They would also
manufacture UNS C70600 End Caps following all the national and international standards, and would
supply them at a competitive price. Apart from that, they also
focus on properly packing the Copper Nickel 90/10 Stub End so that they do not get damaged during the transportation process.
Renowned manufacturers always adhere to their timelines and most of
them offer doorstep deliveries too.
UNS C70600 PIPE FITTINGS SPECIFICATIONS
Supplier of CW352h Saddle and CuNi 90/10 Concentric Reducers, Third
Party Inspection and EN 102043.1 Reports
| Standard Specification | MSS-SP43, EEMUA-146, DIN86090, DIN86088, MSS-SP97, ASME-B16.9,
DIN28011, MIL-T-16420K |
| Trade Name | Copper Nickel 90/10 Pipe Fittings |
| Other Trade Name | Cuni 90/10 |
| Pressure Rating | - 10Bar, 14BAR, 16BAR, 20BAR
- MIL-T-16420K: Class 200, Class 500, Class 700
- PN10, PN14
|
| Manufacturing size range of Copper Nickel 90/10 Buttweld Fittings | 1/2" - 24"
DN15-DN500
OD 20 to OD 508
or custom |
| Thickness | 1.5 to 15mm |
| Schedule Sizes | SCH5/ 5S, SCH10/ 10S, SCH40/ 40S, STD, SCH80, SCH160 |
| Material Test Certificates (MTC) | All Copper Nickel 90/10 Pipe Fittings material supplied with MT |
TEMPERATURE AND WORKING PRESSURE OF COPPER NICKEL C70600 FITTINGS
| Type of Copper Nickel 90/10 fittings | Size range | 16 bar rating Copper Nickel 90/10 fittings | 20 bar rating Copper Nickel 90/10 fittings |
| | | 38˚C | 50˚C | 75˚C | 100˚C | 38˚C | 50˚C | 75˚C | 100˚C |
| UNS C70600 Butt Weld fittings | 1 inch - 4 inch
30mm - 108mm | Use 20 bar | 20.0 | 19.7 | 18.6 | 17.3 |
| 9010 Copper Nickel Butt Weld fittings | 6in - 36in/
159mm - 914mm | 16.0 | 16.0 | 16.0 | 15.7 | 20.0 | 19.7 | 18.6 | 17.3 |
| ASTM B466 UNS C70600 Socket weld fittings | ½in/ - 2in
16mm - 57mm | Use 20 bar | 20.0 | 19.7 | 18.6 | 17.3 |
| CuNi 90/10 Capillary brazed fittings | ½in/ - 2in
16mm - 57mm | 20.0 | 19.7 | 18.6 | 17.3 |
| Cupro Nickel 90/10 Compression fittings | ½in/ - 2in
16mm - 57mm | - | - | - | - |
COPPER NICKEL 90/10 PIPE FITTINGS SIZES
| NPS | OD (in mm) |
| 1/2 | 21.3 |
| 3/4 | 26.7 |
| 1 | 33.4 |
| 1.1/4 | 42.2 |
| 1.1/2 | 48.3 |
| 2 | 60.3 |
| 2.1/2 | 73 |
| 3 | 88.9 |
| 3.1/2 | 101.6 |
| 4 | 114.3 |
| 5 | 141.3 |
| 6 | 168.3 |
| 8 | 219.1 |
| 10 | 273.1 |
| 12 | 323.9 |
| 14 | 355.6 |
| 16 | 406.4 |
| 18 | 457.2 |
| 20 | 508 |
| 24 | 609.6 |
COPPER NICKEL 90/10 PIPE FITTINGS CHEMICAL COMPOSITION
| UNS C70600 Fittings | MIL-T-16420K
C70600 | DIN 86019
Cuni 90/10 (2.1972) | EEMUA 144
UNS 7060X | ASTM B466
C70600 | BS 2871
CN 102 | JIS H 3300
C7060 |
|---|
| Ni% | 9.0-11.0 | 9.0-11.0 | 10.0-11.0 | 9.0-11.0 | 10.0-11.0 | 9.0-11.0 |
| Fe% | 1.0-1.8 | 1.5-1.8 | 1.5-2.0 | 1.0-1.8 | 1.0-2.0 | 1.0-1.8 |
| Mn% | Max1.0 | 0.5-1.0 | 0.5-1.0 | Max.1.0 | 0.5-1.0 | 0.2-1.0 |
| C% | Max.0.05 | Max.0.05 | Max.0.05 | Max.0.05 | Max.0.05 | |
| Pb% | Max.0.02 | Max.0.03 | Max.0.01 | Max.0.02 | Max.0.01 | Max.0.05 |
| S% | Max.0.02 | Max.0.015 | Max.0.02 | Max.0.02 | Max.0.05 | |
| P% | Max.0.02 | Max.0.02 | Max.0.02 | Max.0.02 | | |
| Zn% | Max.0.05 | Max.0.15 | Max.0.20 | Max.0.50 | | Max.0.50 |
| Zr% | | Max.0.03 | | | | |
| Others | | Max.0.30 | Max.0.30 | | Max.0.30 | |
| Cu% | Min.86.5 | Balance | Balance | Balance | Balance | Cu+Ni
+Fe+Mn
Min.99.5 |