Tee Branch Pneumatic Parts Compression Copper Pipe Fitting Reducing
Tee Copper
The UNS C70600 Reducer helps to reduce the flow rate in various
equipment, especially where the use of seawater is involved. They
are used in shipbuilding industries as the CuNi 90/10 End Cap shows
good resistance in the seawater environment. This includes
resistance to pitting and stress corrosion cracking, along with
high resistance to crevice corrosion. The CW352h Saddle is also
well-known for its properties which include high weldability,
fabricability, and they resist biofouling too. The CuNi 90/10
Concentric Reducers show good resistance in high temperature
situations and hence they can be found in condensers and heat
exchangers.
While explaining what is Copper Nickel 90/10 Fittings, it is
essential to know where they are used. The UNS C70600 Fittings are
basically fittings made of 90% copper and 10% nickel alloy. It also
contains a trace amount of other materials such as manganese and
iron in its chemical composition. The content of the alloy in the
90/10 Copper Nickel Pipe Fittings help it to gain enhanced strength
and better corrosion resistance. Manufacturers offer the Copper
Nickel 90/10 Tee and other products according to the specified
requirements of the clients. Their shape, size, dimensions, and
surface finishes can be customized as per the application.
Clients should buy 9010 Copper Nickel Equal Tee from experienced
manufacturers, who use expert professionals and advanced technology
in the production process. This would help to enhance the quality
of the ASTM B466 UNS C70600 Reducing Tee and have products with
enhanced lifespan. They would also manufacture UNS C70600 End Caps
following all the national and international standards, and would
supply them at a competitive price. Apart from that, they also
focus on properly packing the Copper Nickel 90/10 Stub End so that
they do not get damaged during the transportation process. Renowned
manufacturers always adhere to their timelines and most of them
offer doorstep deliveries too.
UNS C70600 PIPE FITTINGS SPECIFICATIONS
Supplier of CW352h Saddle and CuNi 90/10 Concentric Reducers, Third
Party Inspection and EN 102043.1 Reports
| Standard Specification | MSS-SP43, EEMUA-146, DIN86090, DIN86088, MSS-SP97, ASME-B16.9,
DIN28011, MIL-T-16420K |
| Trade Name | Copper Nickel 90/10 Pipe Fittings |
| Other Trade Name | Cuni 90/10 |
| Pressure Rating | - 10Bar, 14BAR, 16BAR, 20BAR
- MIL-T-16420K: Class 200, Class 500, Class 700
- PN10, PN14
|
| Manufacturing size range of Copper Nickel 90/10 Buttweld Fittings | 1/2" - 24"
DN15-DN500
OD 20 to OD 508
or custom |
| Thickness | 1.5 to 15mm |
| Schedule Sizes | SCH5/ 5S, SCH10/ 10S, SCH40/ 40S, STD, SCH80, SCH160 |
| Material Test Certificates (MTC) | All Copper Nickel 90/10 Pipe Fittings material supplied with MT |
TEMPERATURE AND WORKING PRESSURE OF COPPER NICKEL C70600 FITTINGS
| Type of Copper Nickel 90/10 fittings | Size range | 16 bar rating Copper Nickel 90/10 fittings | 20 bar rating Copper Nickel 90/10 fittings |
| | | 38˚C | 50˚C | 75˚C | 100˚C | 38˚C | 50˚C | 75˚C | 100˚C |
| UNS C70600 Butt Weld fittings | 1 inch - 4 inch
30mm - 108mm | Use 20 bar | 20.0 | 19.7 | 18.6 | 17.3 |
| 9010 Copper Nickel Butt Weld fittings | 6in - 36in/
159mm - 914mm | 16.0 | 16.0 | 16.0 | 15.7 | 20.0 | 19.7 | 18.6 | 17.3 |
| ASTM B466 UNS C70600 Socket weld fittings | ½in/ - 2in
16mm - 57mm | Use 20 bar | 20.0 | 19.7 | 18.6 | 17.3 |
| CuNi 90/10 Capillary brazed fittings | ½in/ - 2in
16mm - 57mm | 20.0 | 19.7 | 18.6 | 17.3 |
| Cupro Nickel 90/10 Compression fittings | ½in/ - 2in
16mm - 57mm | - | - | - | - |
COPPER NICKEL 90/10 PIPE FITTINGS SIZES
| NPS | OD (in mm) |
| 1/2 | 21.3 |
| 3/4 | 26.7 |
| 1 | 33.4 |
| 1.1/4 | 42.2 |
| 1.1/2 | 48.3 |
| 2 | 60.3 |
| 2.1/2 | 73 |
| 3 | 88.9 |
| 3.1/2 | 101.6 |
| 4 | 114.3 |
| 5 | 141.3 |
| 6 | 168.3 |
| 8 | 219.1 |
| 10 | 273.1 |
| 12 | 323.9 |
| 14 | 355.6 |
| 16 | 406.4 |
| 18 | 457.2 |
| 20 | 508 |
| 24 | 609.6 |
COPPER NICKEL 90/10 PIPE FITTINGS CHEMICAL COMPOSITION
| UNS C70600 Fittings | MIL-T-16420K
C70600 | DIN 86019
Cuni 90/10 (2.1972) | EEMUA 144
UNS 7060X | ASTM B466
C70600 | BS 2871
CN 102 | JIS H 3300
C7060 |
|---|
| Ni% | 9.0-11.0 | 9.0-11.0 | 10.0-11.0 | 9.0-11.0 | 10.0-11.0 | 9.0-11.0 |
| Fe% | 1.0-1.8 | 1.5-1.8 | 1.5-2.0 | 1.0-1.8 | 1.0-2.0 | 1.0-1.8 |
| Mn% | Max1.0 | 0.5-1.0 | 0.5-1.0 | Max.1.0 | 0.5-1.0 | 0.2-1.0 |
| C% | Max.0.05 | Max.0.05 | Max.0.05 | Max.0.05 | Max.0.05 | |
| Pb% | Max.0.02 | Max.0.03 | Max.0.01 | Max.0.02 | Max.0.01 | Max.0.05 |
| S% | Max.0.02 | Max.0.015 | Max.0.02 | Max.0.02 | Max.0.05 | |
| P% | Max.0.02 | Max.0.02 | Max.0.02 | Max.0.02 | | |
| Zn% | Max.0.05 | Max.0.15 | Max.0.20 | Max.0.50 | | Max.0.50 |
| Zr% | | Max.0.03 | | | | |
| Others | | Max.0.30 | Max.0.30 | | Max.0.30 | |
| Cu% | Min.86.5 | Balance | Balance | Balance | Balance | Cu+Ni
+Fe+Mn
Min.99.5 |