AISI ATSM 2B 8K Stainless Steel Coil Use for Industry
Grades 321 and 347 are the basic austenitic 18/8 steel (Grade 304)
stabilized by Titanium (321) or Niobium (347) additions. These
grades are used because they are not sensitive to intergranular
corrosion after heating within the carbide precipitation range of
425-850 °C. Grade 321 is the grade of choice for applications in
the temperature range of up to about 900 °C, combining high
strength, resistance to scaling and phase stability with resistance
to subsequent aqueous corrosion. Grade 321H is a modification of 321 with higher carbon content, to
provide improved high-temperature strength.A limitation with 321 is that titanium does not transfer well
across a high-temperature arc, so it is not recommended as a
welding consumable. In this case grade 347 is preferred - the
niobium performs the same carbide stabilization task but can be
transferred across a welding arc. Grade 347 is, therefore, the
standard consumable for welding 321. Grade 347 is only occasionally
used as parent plate material.Like other austenitic grades, 321 and 347 have excellent forming
and welding characteristics, are readily brake or roll-formed and
have outstanding welding characteristics. Post-weld annealing is
not required. They also have excellent toughness, even down to
cryogenic temperatures. Grade 321 does not polish well, so is not
recommended for decorative applications.Grade 321H is a modification of 321 with higher carbon content, to
provide improved high-temperature strength.A limitation with 321 is that titanium does not transfer well
across a high-temperature arc, so it is not recommended as a
welding consumable. In this case grade 347 is preferred - the
niobium performs the same carbide stabilization task but can be
transferred across a welding arc. Grade 347 is, therefore, the
standard consumable for welding 321. Grade 347 is only occasionally
used as parent plate material.Like other austenitic grades, 321 and 347 have excellent forming
and welding characteristics, are readily brake or roll-formed and
have outstanding welding characteristics. Post-weld annealing is
not required. They also have excellent toughness, even down to
cryogenic temperatures. Grade 321 does not polish well, so is not
recommended for decorative applications. | Standard: | UNS N08330 | Grade: | 330 |
|---|
| Certificate: | Mill MTC ,Third Party Inspection | Process: | Hot Rolled |
|---|
| Thickness: | 2mm- 120mm | Width: | 10mm-2030mm |
|---|
| Length: | Max 18000mm | Surface Finish: | No.1 |
|---|
FAQ
Q: Would you provide samples For free?
A: Yes . with on stock specification We provide samples For Free .
Freight charge collect
Q: What information should i provide to source for the right
products ?
A: Material grade, width, thickness, coating and Purchase quantity
, Expected lead time ,etc
Q: What are the shipping ports?
A:Under normal circumstances, we ship from Shanghai, Tianjin,
Qingdao, Ningbo ports, you
can choose other ports according to your needs.
Q: About product prices?
A:Prices vary from period to period due to cyclical changes in the
price of raw materials.
Q: How long does your delivery time take?
A:In general, our delivery time is within 5-45 days, and may be
delayed if the demand is extremely
large or special circumstances occur.
Q: Can I visit your location?
A: Of course, we welcome customers from all over the world to visit
our factory. However, some
of the plants are not open to the public.
Q: Does the product have quality inspection before loading?
A: Of course, all our products are strictly tested for quality
before packaging, and unqualified
products will be destroyed.
Q: How to pack the products?
A:The inner layer has a waterproof paper outer layer with iron
packaging and is fixed with a fumigation
wooden pallet. It can effectively protect products from corrosion
during ocean transportation.
Q: What is your working time?
A: In general, our online service time is Beijing time: 8:00-22:00,
after 22:00,
we will reply to your inquiry during the next working day.
|