Hot Sale CrFeAl 145 Supplier 0cr25al5 Wire for Heating Electric
Stove
FeCrAl alloy has the characteristic of high resistivity,low
temperature resistance coefficient,high operating temperature,good
anti-oxidation and anti-corrosion under high temperature.
It is widely used in industrial furnace, household appliances,
industry furnace, metallurgy, machinery, aircraft, automotive,
military and other industries producing heating elements and
resistance elements.
With the characteristics of high resistance, low coefficient of
electric resistance, High operating temperature, good corrosion
resistance under high temperature.
It is mainly used in electric locomotive, diesel locomotive, metro
vehicle and high Speed moving car etc brake system brake resistor,
electric ceramic cooktop, industrial furnace.
2. Specification
1). Locomotive resistance strip:
Thickness: 0.6mm-1.5mm
Width: 60mm-90mm
2). Electric ceramic cooktop resistance strip:
Thickness: 0.04mm-1.0mm
Width: 5mm-12mm
Thickness&Width: (0.04mm-1.0mm)× 12mm(above)
3). Low resistance ribbon:
Thickness&Width: (0.2mm-1.5mm)*5mm
4). Industrial furnace ribbon:
Thickness: 1.5mm-3.0mm
Width: 10mm-30mm
3. Features
Stable performance; Anti-oxidation; Corrosion resistance; High
temperature stability; Excellent coil-forming ability; Uniform and
beautiful surface condition without spots.
4. Packing detail
Spool, coil, wooden case(as per client's requiryment)
5. Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Stable properties in high temperature;
5). Fast delivery;
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max |
| 0.12 | 0.025 | 0.025 | 0.70 | Max 1.0 | 13.0~15.0 | Max 0.60 | 4.5~6.0 | Bal. | - |
Mechanical Properties
| Max Continuous Service Temp | 980ºC |
| Resisivity at 20ºC | 1.28 ohm mm2/m |
| Density | 7.4 g/cm3 |
| Thermal Conductivity | 52.7 KJ/m@h@ºC |
| Coefficient of Thermal Expansion | 15.4×10-6/ºC |
| Melting Point | 1450ºC |
| Tensile Strength | 637~784 Mpa |
| Elongation | Min 12% |
| Section Variation Shrink Rate | 65~75% |
| Repeatedly Bend Frequency | Min 5 times |
| Continuous Service Time | - |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |
Temperature Factor of Electrical Resistivity
| 20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 500ºC | 600ºC | 700ºC | 800ºC | 900ºC | 1000ºC |
| 1 | 1.005 | 1.014 | 1.028 | 1.044 | 1.064 | 1.090 | 1.120 | 1.132 | 1.142 | 1.150 |
Specifications
0Cr25AL5 FeCrAl resistance heating wire
1.Fe-Cr-Al alloy
2.GB/T 1234-95
3.Anti-oxidation
0Cr25AL5 FeCrAl resistance heating wire
Iron-chromium-aluminium (FeCrAl) alloys
FeCrAl alloys are characterized by excellent oxidation resistance
and very good form stability resulting in long element life.They
are typically used in electrical heating elements in industrial
furnaces and home appliances.
FeCrAl alloys have higher service temperature then NiCr Alloys and
much lower prices.But they have lower stability and flexibility,
easily to be fragile after a time circle.