0.12*300mm Fecral Alloy 1cr13al4 Resistor Heating Foil for Etching
resistance
1. Description
FeCrAl Resistance Alloy belongs to electric heating alloy. FeCrAl
alloy contains a large number of chromium and aluminum elements, it
has excellent high temperature oxidation resistance, its
temperature can reach 1400 degrees Celsius.
2. Advantage
FeCrAl Heating alloy has also joined the rare earth elements,
changing the composition of the oxide film, the organizational
structure and improving the strength and ductility of the oxide
film, the increase in density and adhesion, thereby enhancing the
antioxidant capacity of the alloy, extended heating element life.
3. Forming
It exists in the form of strip, round wire, ribbon wire, sheet,
tape, rod and plate.
4. Application
They are mainly used in electric locomotive, diesel locomotive,
metro vehicle and high speed moving car etc brake system brake
resistor, electric ceramic cooktop, industrial furnace.
4.1. Locomotive Resistor Alloy
The locomotive resistance strip is used in braking system of
electric power, engine, subway in resistance cabinet.
The available grade: 0Cr13Al4, 1Cr15Al5
Regular size: (0.6mm--1.5mm)*(60mm--90mm)
4.2. Home Appliances
The electric heating strip is used in electric blanket, hair dryer,
rice cookers, electric kettle, electric ceramic cooktop etc.
The available grade: 0Cr21Al6, 0Cr25Al5
Regular size: (0.04mm--0.1mm)*(5mm-12mm)
(0.04mm--0.1mm)*12mm(above)
4.3. Industrial Furnace Strip
The FeCrAl resistance strip is used heat treatment furnace, melting
furnace, dosing and holding furnace, dental furnace, diffusion
furnace, laboratory furnace.
The available grade: 0Cr13Al4, 0Cr21Al6, 0Cr25Al5, 0Cr20Al5,
0Cr23Al5
Regular size: (1.5mm--3mm)*(10mm--30mm)
4.4. FeCrAl foil for catalytic converter
The FeCrAl resistance foil is used in catalytic converter of
automobile, motorcycle for purifying gas.
The available grade: 0Cr20Al5, 0Cr25Al5
Regular size: (0.06mm--0.08mm)*(10mm--30mm)
| Properties/Grade | 1Cr13Al4 | 0Cr21Al4 | 0Cr21Al6 | 0Cr23Al5 | 0Cr25Al5 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Main Chemical composition(%) | Cr | 12.0-15.0 | 18.0-21.0 | 19.0-22.0 | 22.5-24.5 | 23.0-26.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 3.0-4.2 | 5.0-7.0 | 4.2-5.0 | 4.5-6.5 | 5.0-7.0 | 6.0-7.0 |
| Fe | Balance | Balance | Balance | Balance | Balance | Balance | Balance |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| | | | | | | Nb:0.5 | Mo:1.8-2.2 |
| Max. continuous service temp. of element | 950 | 1100 | 1250 | 1250 | 1250 | 1350 | 1400 |
| Resistivity at 20oC (μ Ω @ m) | 1.25+-0.08 | 1.23+-0.06 | 1.42+-0.07 | 1.35+-0.07 | 1.42+-0.06 | 1.45+-0.07 | 1.53+-0.07 |
| Density (g/cm3) | 7.4 | 7.35 | 7.16 | 7.25 | 7.1 | 7.1 | 7.1 |
| Thermal conductivity(KJ/m@ h@ ºC) | 52.7 | 46.9 | 63.2 | 60.2 | 46.1 | 46.1 | 45.2 |
| Coefficient of lines expansion(α × 10-6/ºC) | 15.4 | 13.5 | 14.7 | 15 | 16 | 16 | 16 |
| Melting point (approx. )( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Elongation at rupture (%) | ≥16 | ≥12 | ≥12 | ≥12 | ≥12 | ≥12 | ≥10 |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic properties | magnetic | magnetic | magnetic | magnetic | magnetic | magnetic | magnetic |