Soft Annealed Catalytic Converter FeCrAl Alloy For Heat Element

Brand Name	TANKII
Model Number	X8cral 20-6
Certification	ISO9001
Place of Origin	Shanghai
Minimum Order Quantity	50kg
Payment Terms	L/C, T/T, Western Union
Supply Ability	90+ton+per month
Delivery Time	8-15 days
Packaging Details	to wind with thin film, bubble film,carton,wooden pallet or case
material	fecral
condition	soft annealed
surface	bright
shape	foil,strip,sheet

Detailed Product Description

X8cral 20-6 Catalytic Converter Foil

Nominal Analysis

21.00 Cr, 6.00 Al, Bal. Fe

Max contineous working temperature: 1250º C.

Melting Temperature: 1500º C

Thickness 0.05~0.1mm, width 1-1000mm

Usage: Catalytic converters

Material 1.4767, DIN 17470

Brand name		1Cr13Al4	0Cr25Al5	0Cr21Al6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb	0Cr27Al7Mo2
Main chemical composition%	Cr	12.0-15.0	23.0-26.0	19.0-22.0	22.5-24.5	18.0-21.0	21.0-23.0	26.5-27.8
	Al	4.0-6.0	4.5-6.5	5.0-7.0	4.2-5.0	3.0-4.2	5.0-7.0	6.0-7.0
	RE	opportune amount	opportune amount	opportune amount	opportune amount	opportune amount	opportune amount	opportune amount
	Fe	Rest	Rest	Rest	Rest	Rest	Rest	Rest
							Nb0.5	Mo1.8-2.2
Max.continuous service temp.of element (ºC)		950	1250	1250	1250	1100	1350	1400
Resistivity μΩ.m,20ºC		1.25	1.42	1.42	1.35	1.23	1.45	1.53
Density (g/cm3 )		7.4	7.10	7.16	7.25	7.35	7.10	7.10
Thermal conductivity KJ/m.h.ºC		52.7	46.1	63.2	60.2	46.9	46.1	45.2
Coefficient of lines expansion α×10-6/ºC		15.4	16.0	14.7	15.0	13.5	16.0	16.0
Melting pointºC		1450	1500	1500	1500	1500	1510	1520
Tensile strength Mpa		580-680	630-780	630-780	630-780	600-700	650-800	680-830
Elongation at rupture %		>16	>12	>12	>12	>12	>12	>10
Variation of area %		65-75	60-75	65-75	65-75	65-75	65-75	65-75
Repeat bending frequency(F/R)		>5	>5	>5	>5	>5	>5	>5
Hardness(H.B.)		200-260	200-260	200-260	200-260	200-260	200-260	200-260
Micrographic structure		Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite
Magnetic properties		Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic	Magnetic

Fecral alloy is high resistance and electrical heating alloy. Fecral alloy can reach process temperature of 2192 to 2282 F, corresponding to oa resistance temperature of 2372 F.

It is normally used in electrical furnace, glass top hobs, quartz tube heaters, resistors, catalytic converter,heating elements etc.

Product Tags: Catalytic Converter FeCrAl Alloy Soft Annealed FeCrAl Alloy Bright Heat Element FeCrAl Alloy

Related Products

FeCrAl Alloy Wire 0.6mm 1.2mm High Temperature Resistance Heating for sale


From:	Enter your Email please. Your email is incorrect!
To:	Shanghai Tankii Alloy Material Co.,Ltd
Subject:	Subject is empty!
Message:	Characters Remaining: (80/3000) Please enter 20 to 3000 characters to contact this supplier!

Soft Annealed Catalytic Converter FeCrAl Alloy For Heat Element

Soft Annealed Catalytic Converter FeCrAl Alloy For Heat Element

FeCrAl Alloy Wire 0.6mm 1.2mm High Temperature Resistance Heating

0Cr21Al6Nb FeCrAl Alloy Heating Wire 1250ºC Max Temp

FeCrAl Alloy Wire 1Cr13Al4 High Resistance Heating Element

FeCrAl Alloy Wire 0Cr25Al5 High Temperature Resistance Coil

Hot Sale 0.1-10mm 1Cr13Al4 Fecral Alloy Electric Heating Wire

FeCrAl Alloy 0Cr25Al5 Chemical Heating Wires Bright Surface