1. Description
With the characteristics of high resistance, low coefficient of
electric resistance, High operating temperature, good corrosion
resistance under high temperature, It is widely used in industrial
electric furnace, household electrical appliance and Far infrared
ray device.
2. Specification
Wire:
Diameter: 0.15mm-8.0mm
Strip:
Thickness: 0.6mm-1.5mm
Width: over 40mm
3. Usage
It is mainly used in electric locomotive, diesel locomotive, metro
vehicle and high speed moving car etc brake system brake resistor,
electric ceramic cooktop, industrial furnace.
4. Features
Stable performance; Anti-oxidation; Corrosion resistance; High
temperature stability; Excellent coil-forming ability; Uniform and
beautiful surface condition without spots.
5. Packing detail
1) Coil (plastic spool) + compressed ply-wooden case + pallet
2) Coil (plastic spool) + carton + pallet
6. Products and services
1). Pass: ISO9001 certification, and SO14001cetification;
2). Fine after-sale services;
3). Small order accepted;
4). Stable properties in high temperature;
5). Fast delivery;
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
| Max |
| 0.05 | 0.025 | 0.025 | 0.70 | Max 0.6 | 21.0~23.0 | Max 0.60 | 5.0~7.0 | Bal. | Nb 0.5 |
| Max Continuous Service Temp | 1350ºC |
| Resistivity at 20ºC | 1.45 ohm mm2/m |
| Density | 7.1 g/cm3 |
| Thermal Conductivity | 46.1 KJ/m·h·ºC |
| Coefficient of Thermal Expansion | 16.0×10-6/ºC |
| Melting Point | 1510ºC |
| Tensile Strength | 637~784 Mpa |
| Elongation | Min 12% |
| Section Variation Shrink Rate | 65~75% |
| Repeatedly Bend Frequency | Min 5 times |
| Continuous Service Time | - |
| Hardness | 200-260HB |
| Micrographic Structure | Ferrite |
| Magnetic Property | Magnetic |
| 20ºC | 100ºC | 200ºC | 300ºC | 400ºC | 500ºC | 600ºC | 700ºC | 800ºC | 900ºC | 1000ºC | 1100ºC | 1200ºC |
| 1 | 0.997 | 0.996 | 0.994 | 0.991 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 | 0.990 |
Standard Specification:
| Grade | Main chemical composition | Hightest temperature ℃ | Rrsistivity
µΩ.m | Melting point ℃ | Tensile strength N/mm² | Elogation
% | Working life
h/℃ | Magnetic
properties |
| | Cr | Al | Ni | Fe | | | | | | | |
| OCr21Al4 | 17-21 | 3-4 | - | - | 1100 | 1.23±0.06 | 1500 | 750 | ≥12 | ≥80/1250 | magnetic |
| OCr25Al5 | 23-26 | 4.5-6.5 | - | - | 1250 | 1.42±0.07 | 1500 | 750 | ≥12 | ≥80/1300 | magnetic |
| OCr21Al6Nb | 21-23 | 5-7 | - | - | 1350 | 1.43±0.07 | 1510 | 750 | ≥12 | ≥50/1350 | magnetic |
| OCr27Al7Mo2 | 22-24 | 5-7 | - | - | 1400 | 1.53±0.07 | 1520 | 750 | ≥10 | ≥50/1350 | magnetic |
| KSC | 26.8-27.8 | 6-7 | - | - | 1350 | 1.44±0.05 | 1510 | 750 | ≥16 | ≥60/1350 | magnetic |
| Cr20Ni80 | 20-23 | - | Rest | ≤1.0 | 1200 | 1.09±0.05 | 1400 | 750 | ≥20 | ≥80/1200 | Non-magnetic |
| Cr30Ni70 | 30 | - | Rest | ≤1.0 | 1250 | 1.18±0.05 | 1380 | 750 | ≥20 | ≥50/1250 | Non-magnetic |
| Cr15Ni60 | 15-18 | - | 55 | Rest | 1150 | 1.12±0.05 | 1390 | 750 | ≥20 | ≥80/1150 | Non-magnetic |
| Cr20Ni35 | 18-21 | - | 35 | Rest | 1100 | 1.04±0.05 | 1390 | 750 | ≥20 | ≥80/1100 | Weak magnetic |
| Cr20Ni30 | 20 | - | 32 | Rest | 1100 | 1.04±0.05 | 1390 | 750 | ≥20 | ≥80/1100 | Weak magnetic |