2×6.0mm² (PV1-F / H1Z2Z2-K)
(NO.7194104) |
| General characteristics: |
|
| Appllcation: |
Specifically designed to connect photovoltaic system components
inside and outside buildings
and facilities under high mechanical demands and extreme weather
conditions. |
| Cable Construction: |
| Conductor | |
|
| Metarial: | Tinned annealed copper |
| Area(mm²) : | 2×6.0 |
| Construction(N/mm) : | 84/0.30 |
| Conductor(Dia./mm) : | 3.17 | |
| Insulation | 120℃ XLPE |
| Standard thickness (mm) : | 0.75 |
| Standard diameter (mm) : | 4.67±0.1 |
| Jacket | 120℃ XLPE, Black |
| Standard thickness (mm) : | 1.05 |
| Outer diameter (mm) : | (7.0±0.2)×(14.5±0.2) |
| Weight rated | 102.6 |
| Making | ZION COMMUNICATION PV1-F / H1Z2Z2-K 2x6.0mm²
UV Res DC 1.5KV AC 0.6/1KV SOLAR CABLE |
| | | | | | | |
| Package: |
| BOX (art.code ZC-100-2×6.0mm/ZC-500-2×6.0mm) |
|
| Size: 310x 310x100mm |
| PALLET (art.code ZC-100-100-2×6.0mm) |
| Size: 1100x1100mm |
| Amount of boxes on one pallet: | |
| Weight of total pallet: | |
| Cable length pallet: | |
| |
| Electrical properties |
| Nominal Voltage: | PV1-F: DC 1.0KV AC 0.6/1.0KV
H1Z2Z2-K: DC 1.5KV AC 1.0/1.0KV |
| Ambient Temperature: | -40℃~+90℃ |
| Max.Temperature at conductor: | +120℃ |
| Service life: | ＞25 years ( -40℃~+90℃) |
| Voltage: | 600/1000V |
| Temperature: | -40~90℃ |
| Conductor resistance (20℃): | 3.39Ω/km |
| Insulation resistance (70℃): | ≥1000 MΩ/km |
| Withstand voltage(V/5min) | AC6500 |
| Speak voltage(V/5min) | AC6500 |
| Min bending radius(mm) | 4*D |
| |
| Main performance parameter of finished cable |
| Voltage test of finished cable |
| Min.time of dipping in water | ≥1(h) |
| Testing voltage (AC) | 6500(V) |
| Min.voltage applying time at one time | 5(min) |
| Test result | no breakdown |
| Sheated surface resistance |
| Length of specimen: | 250mm |
| Test result | ≥109Ω |
| Penetrate the insulation resistance |
| Temperature | 20℃ |
| Test result | ≥1014Ω |
| High temperature stress |
| Temperature | 140℃ |
| A: with 1.2 Voltage test | A: No breakdown |
| B: deep pressure | B: Wall thickness 50% |
| Damp-heat test |
| Temperature | 90℃ |
| Humidity | 0.85 |
| Aging before and after the tenslle strength of Change | ≤30% |
| Aging before and after the elongation at break of Change | ≤-30% |
| |
| Acid-alkali Resistance |
| Min.time of dipping in | 168h |
| Aging before and after the tensile strength of Change | ≤-30% |
| Elongation | ≥100 |
| Low-temperature bending |
| Temperature | -40℃ |
| Time | 16h |
| Test result | No crack |
| Ozone resistance |
| Ozeone concentration % | (200±50)x10-6 |
| Time | 72h |
| Test result | No crack |
| Heat schrinkable jacket test |
| Test result | ≤2% |
| Flame retardant-Vertical burn | |
| Flxture on the lower edge from the starting point and carbonization | ≥50mm |
| Burning fuel downward from the lower edge of bottom fixture | ≤540mm |
| Halogen content of non-metallic materials |
| Test result | |
| Chlorine and bromine content | HCL≤0.5HBr≤0.5% |
| Fluoride content | F≤0.1% |
| The inner layer of insulation and sheath of the mechanical
properties |
| Test result | |
| Aging before tensile strength | 8.0N/mm² |
| Aging before elongation | 1.25 |
| Aging before and after the tensile strength of change | -30% |
| Aging before and after the elongation at break of change | -30% |
| Hot extension |
| Temperature | 200℃ |
| Test result-The inner layer of insulation and sheath | |
| Elongation under load | ≤100% |
| Elongation after unloading | ≤25% |