MoSi2 Molybdenum Products Molybdenum Heating Elements for
Disilicide Furnace
Product Description
MoSi2 heating elements is made from Molybdenum Disilicide with
excellent thermal resistance. It can be used in air and
various gases environments. Working temperature of MoSi2 heating
element is 1300C to 1800C and it has been widely used as
heaters in high temperature furnaces and kilns of metallurgy,
glass, ceramic refractory, crystal electronic device, industrial
furnace manufacture and chemical industry field.
Types of MoSi2 Heating Elements
1. According to temperature: 1700C and 1800C
2. According to Shape: U, W, I, UL, WL, Spiral types.
MoSi2 Heating Elements Standard Size:
(Hot zone dia / Cold zone dia)
3/6mm, 4/9mm, 6/12mm, 9/18mm, 12/24mm.
Chemical property of MoSi2
High temperature oxidation resistance:
When MoSi2 heating elements are used at high temperature and under
oxidation circumstance, a dense layer of quartz (SiO2) is generated
on the surface of the element to prevent it from further oxidation.
When the temperature of element is over 1700ºC, the SiO2 protecting
film whose melting point is 1710ºC will be melted. Due to its
surface tension, SiO2 agglomerate() into drops and lose protection.
The SiO2 protecting film is formed again when the element continues
to be used under the oxidation circumstance.
It must be pointed out is that the MoSi2 heating element cannot be
used in the temperature between 400ºC to 700 ºC for long time.
Otherwise, the element will be pulverized because of the strong
low-temperature oxidation.
Resistance characters
MoSi2 heating elements have good resistance characteristic, so it
is an ideal heating material to replace traditional heating
elements.
At room temperature, its resistivity is very low, with the increase
of temperature, the resistance increases sharply. The advantages of
heating up fast and low power consumption are obvious.
In normal operating circumstances, the resistance of the element is
constant, so the old and new components can be mixed.
Molybdenum MoSi2 Heating Elements' Application:
Item | Name | Distinction criterion | Specification | Using range |
Heating elements | 1700 type | Element operating temperature 1700ºC is acceptable | Le Φ 6-12W type/U type/L type/all kinds of hetero type / stripe shape | high temperature electric resistance furnace |
1800 type | Element operating temperature 1800ºC is acceptable |
1800J type | Element operating temperature≥1800ºC | Le Φ 3-12W type | Special,high temperature and high-power electric resistance furnace |
1800T type | Element operating temperature≤1800ºC | Le Φ 3-12W type U type | Not oxidized special air high temperature electric resistance
furnace |
Atmosphere influence on the MoSi2 heater's operating
temperature:
Atmosphere | The max element temperature(ºC) |
| 1700type | 1800type |
Air | 1700 | 1800 |
N2 | 1600 | 1700 |
He Ar Ne Argon, Helium | 1600 | 1700 |
Dry Hydrogen(dew point) -80ºC | 1150 | 1150 |
Wet Hydrogen(Dew point) -20ºC | 1450 | 1450 |
mixed gas(e . g . 10%CO2, 50%CO, 15% H2) | 1600 | 1700 |
mixed gas(e . g . 40%CO2 , 20%CO) | 1400 | 1450 |
Cracked and partly burnt ammonia | 1400 | 1450 |
Physics Characters of MoSi2
Bulk density | Bending strength | Hardness | Apparent porosity | Drawing water rate | Thermal elongation rate |
5.6~5.8g/cm3 | 20MPa(20ºC) | (hv)570kg/mm² | 0.5~2.0% | 0.5% | 4% |
Recommend surface load:
Furnace Temp(°c) | 1400 | 1500 | 1600 | 1650 | 1700 |
Surface load of hot zone(W/cm²) | <18 | <15 | <12 | <10 | <8 |
Picture show: