Size 74x84x84mm Copper Based Alloys QBe2 Beryllium C17200 Flat Bar
|
Size 74*84*84mm copper based alloy QBe2 Beryllium copper alloy C17200 flat bar
Common Name: C17200, alloy25, CuBe2, QBe2.0, DIN 2.1247
International Specification:
Properties The best combination of characteristics of the copper-based alloy The copper-beryllium alloys have a wide combination of mechanical and electrical properties which is unique for copper alloys. The mechanical strength achieved after heat treatment ranks highest amongst all the copper alloy materials and is combined with a high electrical conductivity which outperforms that of bronzes.
High Strength & Elastic Modulus Beryllium Copper alloys can achieve very high mechanical properties after heat treatment, up to 1500 Mpa in tensile strength and hardness as high as 450 Vickers. The strength of these alloys allow for the design of smaller, lighter components that can endure high bending stresses when used as springs material.
Bending Formability Beryllium Copper can be formed into complicated shapes in an annealed or cold-worked temper. The highest mechanical properties can be achieved with proper heat-treatment after forming.
High Fatigue Strength Beryllium Copper exhibits excellent resistance to fatigue under reverse bending (up to 300 MPa) which qualifies its use in applications where other alloy fail to provide the same level of reliability.
High Electrical conductivity Beryllium Copper exhibit a high electrical conductivity ranges from 22 to 70% IACS depending on the alloys and temper. Beryllium Copper is often used as high current density spring material.
Heat treatment Heat treatment is the most important process for this alloy system. While all copper alloys are hardenable by cold working, beryllium copper is unique in being hardenable by a simple low temperature thermal treatment. It involves two basic steps. The first is called solution annealing and the second, precipitation or age hardening.
Solution Annealing For the typical alloy CuBe1.9 (1.8- 2%) the alloy is heated between 720°C and 860°C. At this point the contained beryllium is essentially “dissolved” in the copper matrix (alpha phase). By rapidly quenching to room temperature this solid solution structure is retained. The material at this stage is very soft and ductile and can be readily cold worked by drawing, forming rolling, or cold heading. The solution annealing operation is part of the process at the mill and is not typically used by the customer. Temperature, time at temperature, quench rate, grain size, and hardness are all very critical parameters and are tightly controlled by ohmalloy.
Age Hardening Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.
Application Our alloys combine a range of properties particularly suited to meet the exacting requirements of many applications in the automotive, electronic, aeronautical, Oil&Gas, watch, electro-chemical industries, etc. Beryllium Copper is widely used in those fields as contact springs in various applications like connectors, switches, relays, etc Exhibition Customer Photos Testing Equirement Package Shipment
FAQ What is your working time? Monday-Saturday : 7:30AM-17:00PM (Beijing time, GMT+08.00) We have public holiday during May.1-3, Oct.1-7 and Chinese New Year holiday . For detail, please see our update holiday notice. During these period, if you have a demand, Please send me an email.
Do you provide free samples? Yes, we can provide a free sample for testing,buyer should bear all the shipping costs.
What is your payment terms? T/T,L/C,D/A,D/P,,MoneyGram,Paypal
What is the lead time? Usually sample lead time is 7 days after payment has been confirmed. Normal order is 10-30days,it depends on customers' quantity.
|
Product Tags: QBe2 Beryllium Copper Alloy Bar Copper Alloy C17200 Flat Bar Copper Based Alloys Bar 84mm |
![]() |
C18150 / CuCr1Zr Square Rod 20*20*1000mm For Heating Application |
![]() |
High Strength C17200 Beryllium Plate 140 X 140 X 1800mm For Switch Parts |
![]() |
540 X 540X 2340mm Beryllium Copper Plates CuBe2 C17200 For Electrical Switch |
![]() |
C17200 C17500 C17510 Beryllium Copper Plate CuBe2 Square Plate / Sheet |
![]() |
C18150 Chromium Zirconium Copper Rectangular Bar 15x15x200mm |
![]() |
Size 74x84x84mm Copper Based Alloys QBe2 Beryllium C17200 Flat Bar |